Bulk metallic glass (BMG) samples are amalgamated by high-energy ball milling using the general formula (Ni75Cr15Si10)100−xTix (labelled as NCSTx, where x = 0,4, 8 and 12 at.%). The crystallinity and ...phase attribution properties of nickel (Ni), chromium (Cr), silicon (Si) and titanium (Ti) are scrutinized using the XRD analysis. The trend related to glass-forming ability (ΔT) and the GFA parameter (γ) is NCST8 > NCST12 > NCST4 > NCST0, which confirms that NCST8 sample shows superior glass-forming ability. The reduced glass transition temperature (Trg) for all the present BMG systems is greater than 0.5, which offers its good thermal stability and glass-forming ability (GFA). Corrosion studies suggested that a sample, having dynamic nature towards corrosion resistance and potential (Ec) (NCST8, (Ni75Cr15Si10)92Ti8), exhibits relatively lower values of both ic (4.7 × 10−4 A/cm2) and ip (0.0079 A/cm2), as recommended in potentio-dynamic findings.
Full text
Available for:
BFBNIB, DOBA, GIS, IJS, IZUM, KILJ, KISLJ, NUK, PILJ, PNG, SAZU, UILJ, UKNU, UL, UM, UPUK
Bulk metallic glass (BMG) samples are amalgamated by high-energy ball milling using the general formula (Ni
75
Cr
15
Si
10
)
100−x
Ti
x
(labelled as NCST
x
, where x = 0,4, 8 and 12 at.%). The ...crystallinity and phase attribution properties of nickel (Ni), chromium (Cr), silicon (Si) and titanium (Ti) are scrutinized using the XRD analysis. The trend related to glass-forming ability (ΔT) and the GFA parameter (γ) is NCST
8
> NCST
12
> NCST
4
> NCST
0
, which confirms that NCST
8
sample shows superior glass-forming ability. The reduced glass transition temperature (T
rg
) for all the present BMG systems is greater than 0.5, which offers its good thermal stability and glass-forming ability (GFA). Corrosion studies suggested that a sample, having dynamic nature towards corrosion resistance and potential (E
c
) (NCST
8
, (Ni
75
Cr
15
Si
10
)
92
Ti
8
), exhibits relatively lower values of both i
c
(4.7 × 10
−4
A/cm
2
) and i
p
(0.0079 A/cm
2
), as recommended in potentio-dynamic findings.
Full text
Available for:
BFBNIB, DOBA, GIS, IJS, IZUM, KILJ, KISLJ, NUK, PILJ, PNG, SAZU, UILJ, UKNU, UL, UM, UPUK
Load filters
No result was selected!
Please select the results that you wish to export.
The search was successfully saved.
Editing
The search could not be saved.
Saved searches can be viewed in the list My searches.
The changes made to the saved search were saved successfully.
Save search
Shelf entry
No result was selected!
Adding material to shelf was successful.
Adding material to shelf was partly successful.
Adding material to shelf failed completely.
It was not necessary to add the material to the shelf.
Please select the results that you want to put on shelf!
On shelf the following records have been successfully added:
On shelf the following records have been successfully added: