Dentalna keramika danas je jedan od osnovnih gradivnih materijala u fiksnoj protetici. Naime, povećani estetski zahtjevi potaknuli su nastanak novih keramičkih materijala kako bi se izbjegla upotreba ...metalnog skeleta te dobio potpuno keramički rad s mehaničkim svojstvima koja dovoljno dobro podnose jače okluzalne sile. Od svih dosadašnjih keramičkih materijala cirkonij-oksidna keramika ima najbolja mehanička svojstva i jedino se njome možemo koristiti za, u rasponu, dulje fiksnoprotetske radove. No unatoč tomu, estetska svojstva nisu zadovoljavala jer nije bilo translucentnosti. Zbog toga se na cirkonijev dioksid počelo u slojevima nanositi (slojevati) ostale
keramike. Nakon što se počeo upotrebljavati u dentalnoj medicini, cirkonijev dioksid smatrao se idealnim materijalom za fiksnu protetiku koji će vrlo brzo zamijeniti metal-keramičke radove. No tijekom kliničke uporabe te u studijama in vivo i in vitro pokazalo se da i dalje postoji mnogo problema, unatoč poboljšanjima. U ovom preglednom radu željeli smo otkriti nove spoznaje o cirkonij-oksidnoj keramici i tehničkim postupcima koji bi mogli povećati kliničku uspješnost i dugovječnost radova od toga materijala.
Provider: - Institution: University of Zagreb. School of Dental Medicine. Department of Fixed Prosthodontics. - Data provided by Europeana Collections- Komercijalno čisti titan (CP Ti) dobiven ...hladnim izostatičkim i toplo-vakuumskim tlačenjem (CIP/HVP) postupcima metalurgije praha (PM) dosad nije korišten u stomatološkoj protetici. Svrha je istraživanja istražiti utjecaj obrade površine osnovne konstrukcije iz CP Ti dobivenog postupcima PM na veznu čvrstoću s tri obložne keramike te istražiti mehanička svojstva CP Ti dobivenog PM. Istraživanje je provedeno na 120 uzoraka CP Ti dobivenog metalurgijom praha izrezanih na erozimatu podijeljenih u pet skupina prema načinu obrade površine: 1. neobrađena; 2. pjeskarena Al2O3; 3. naneseno vezno sredstvo; 4. pjeskarena Al2O3 i naneseno vezno sredstvo; 5. djelovanje klorovodične kiseline. Svaka skupina podijeljena je u tri podskupine po osam uzoraka te je na njih napečena određena obložna keramika. Testiranje i izračun vezne čvrstoće provedeni su prema ISO 9693. Površina uzoraka prije i poslije obrade te nakon napečenja keramike i provedenog loma snimljena je SEM-om, EDS-om, izmjerena je hrapavost površine profilometrom te je analizirana površinska struktura XRD-om. Rezultati su pokazali da su mehanička svojstva CP Ti/PM usporediva s konvencionalno dobivenim CP Ti i zadovoljavaju za upotrebu u kliničkoj praksi. Također su sve skupine uzoraka osim Initial Ti skupine 1 i Titankeramik skupina 1, 3 i 5 zadovoljile uvjete vrijednosti vezne čvrstoće (> 25 MPa) postavljenih standardom ISO 9693. Za Duceratin Kiss keramiku optimalna obrada površine uključuje pjeskarenje Al2O3 i nanošenje veznog sredstva, dok je za Initial Ti i Titankeramik obložne keramike dovoljno samo pjeskarenje Al2O3. Nije pronađena statistički značajna razlika vrijednosti vezne čvrstoće između triju vrsta obložnih keramika. Komercijalno čisti titan dobiven postupcima metalurgije praha pokazuje sva svojstva potrebna za upotrebu u kliničkoj praksi.- Introduction: Commercially pure titanium (CP Ti) manufactured by cold isostatic and hot vacuum pressing (CIP/HVP) processes of powder metallurgy has not been used in prosthodontics. The aim was to evaluate the effects of surface modification of CP Ti substructures manufactured by PM processes on bond strength with three veneering ceramics, and the mechanical properties of CP Ti manufactured by PM. Materials and methods: 120 samples of CP Ti manufactured by PM shaped on WEDM were divided into 5 groups according to surface modifications: 1. untreated; 2. sandblasted (Al2O3); 3. applied bonding agent; 4. sandblasted (Al2O3) and applied bonding agent; 5. etched with hydrochloric acid. Each group was divided into 3 subgroups of 8 samples and veneering ceramics was applied. Bond strength evaluation was done according to ISO 9693. The surface of the samples was evaluated before and after modifications, after applying veneering ceramics and bond strength testing with SEM, EDS, the roughness was measured with a profilometer, and surface structural analysis was done by XDR. Results: Dynamic mechanical analysis revealed values of Young's module of elasticity (E) 104 GPa, proof strength (Rp0.2) 503 MPa, tensile strength (Rm) 698. Vickers hardness testing showed microhardness values of (HV 0,1) 167. After initial inspection of surface quality, which was satisfactory, bond strength values were measured and the following results were obtained. The results of bond strength testing showed the following values: for the Duceratin Kiss veneering ceramics values range from 25,6 MPa to 41,2 MPa; for the Initial Ti from 12,7 MPa to 38,5 MPa; for the Titankeramik from 17,3 MPa to 38,5 MPa. ANOVA showed statistically significant differences in bond strength values within a group of veneering ceramics for the Duceratin Kiss group 4, the Initial Ti group 2 and the Titankeramik group 2. No statistically significant differences in bond strength values were found between the veneering ceramics. The SEM, EDS and XRD analyses of samples showed predominantly adhesive fractures between veneering ceramics and metal samples. Surface roughness showed significantly higher values of roughness parameter Ra, Rz and Rmax for sandblasted samples. Pearson correlation coefficient between surface roughness and bond strength values was: the Duceratin Kiss r235 %, the Initial Ti r260 % and the Titankeramik r282 %. Conclusion: CP Ti manufactured by PM can be used in prosthodontics as a metal base material in metal ceramic systems.- All metadata published by Europeana are available free of restriction under the Creative Commons CC0 1.0 Universal Public Domain Dedication. However, Europeana requests that you actively acknowledge and give attribution to all metadata sources including Europeana
Korozijski procesi dentalnih slitina dobro su znani. Za razliku od njih malo se zna o koroziji dentalne keramike i zato je svrha ove studije bila raščlamba kemijske stabilnosti dviju vrsta keramike u ...agresivnome kiselome mediju. Uzorci konvencionalne glinične keramike napečeni su na Co-Cr i Ni-Cr slitinu, a uzorak hidrotermalne keramike na visoko plemenitu zlatnu slitinu. Uzorci su bili pohranjeni u otopinu 10-3 mol/L HCl-a na 50°C 6 mjeseci. Otopine su analizirane nakon 1., 2., 3., i 6. mjeseca. Ioni Na+, K+, Ca2+ i Mg2+ bili su određeni ionskom kromatografijom (IC), a kvantitativne vrijednosti izlučenih Si4+ i Al3+ spektrofotometrijskom metodom. Gubitak težine uzoraka mjeren je analitičkom vagom, a promjena pH otopina pH-metrom.
Rezultati su pokazali da je najjača eluacija iona u prva tri mjeseca, te da je izlučivanje bilo znatno manje nakon toga razdoblja iz svih uzoraka. Najznačajnije izlučivanje iona i gubitak težine pokazao je uzorak s hidrotermalnom keramikom. U svim su otopinama nastale promjene u pH vrijednosti, a stabilizirale su se nakon 3. mjeseca od početka istraživanja.
Zaključak je da zubna keramika nije kemijski stabilna u kiselome mediju.
PDF