Lauzuardy, Jason; Agus Basuki, Eddy; Martides, Erie; Septianissa, Selly; Prawara, Budi; Dedi; Junianto, Endro; Riyanto, Edy
Materiali in tehnologije, 01/2024, Volume: 58, Issue: 2Journal Article
With the goals of protecting boiler tubes from hostile surroundings, increasing thermal efficiency, and minimizing time losses from damage, thermal-spray coating methods for high-temperature operations were created. Ceramic-metal composite materials (e.g., Cr3C2-NiCr) are well known for protecting components from erosion decay in a high-temperature environment. In this investigation, the high-velocity oxy-fuel (HVOF) thermal-spray technique was employed to successfully deposit several variations of feedstocks containing Cr3C2-NiCr and NiCr powders onto a medium-carbon steel substrate, with and without filtering through a 400-mesh screen. Utilizing X-ray fluorescence (XRF), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD), the microstructure features of the deposited coatings were assessed. The experiment results demonstrate that the crystallite and grain sizes of the deposited coatings can be increased by reducing the powder size through a sifting process using a 400-mesh sieve. This procedure also resulted in a coating with a higher density and lower porosity. Furthermore, new compounds including Cr2O3 and MnCr2O4 were formed in the coating layers as indicated by the XRD spectra. These phenomena are in good agreement with the EDS mapping of Cr and O, which reveals highly similar distributions. Manganese was originally a part of the substrate composition. Manganese could diffuse rapidly across the Cr2O3 layer and form the MnCr2O4 compound, indicating the manganese diffusion from the substrate into the Cr3C2-NiCr coating. The formation of MnCr2O4 can be attributed to the prior emergence of the Cr2O3 compound.
Author
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.