The (TiZrHfNbTaMo)C‐15 wt.% Co ceramics with excellent comprehensive properties were successfully prepared by vacuum liquid phase sintering. The effects of WC content on the grain size, microstructure, and mechanical properties were investigated. The results showed that WC was dissolved into (TiZrHfNbTaMo)C phase to form a seven‐component solid solution, and the independent WC phase disappeared. The addition of WC improved the wettability between the ceramic phase and the metal phase and promoted the densification of the ceramics. In addition, WC played a role in refining grains and inhibiting the grains growth to a certain extent. The comprehensive properties of ceramics were improved by solid solution strengthening and high entropy effect. When the WC content was 5 wt.%, the toughness reached the maximum of 9.41 ± 0.15 MPa·m1/2, and the hardness of the ceramic with 10 wt.% WC achieved the highest value of 18.18 ± 0.20 GPa.