Han, Zhenchuan; Wang, Bo; Ren, Bowen; Liu, Yihao; Zhang, Nan; Wang, Zheng; Liu, Jianheng; Mao, Keya
Life (Basel, Switzerland), 07/2022, Volume: 12, Issue: 7Journal Article
Magnesium potassium phosphate cement (MKPC) has attracted considerable attention as a bone regeneration material. However, there are only a few reports on its biomechanical properties. To evaluate the biomechanical properties of MKPC, we compared the mechanical parameters of pedicle screws enhanced with either MKPC or polymethyl methacrylate (PMMA) bone cement. The results show that the maximum pull-out force of the pedicle screws was 417.86 ± 55.57 and 444.43 ± 19.89 N after MKPC cement setting for 30 min and 12 h, respectively, which was better than that of the PMMA cement. In fatigue tests, the maximum pull-out force of the MKPC cement group was 435.20 ± 7.96 N, whereas that of the PMMA cement in the control group was 346.80 ± 7.66 N. Furthermore, the structural characterization analysis of the MKPC cement revealed that its microstructure after solidification was an irregular tightly packed crystal, which improved the mechanical strength of the cement. The maximum exothermic temperature of the MKPC reaction was 45.55 ± 1.35 °C, the coagulation time was 7.89 ± 0.37 min, and the compressive strength was 48.29 ± 4.76 MPa, all of which meet the requirements of clinical application. In addition, the MKPC cement did not significantly inhibit cell proliferation or increase apoptosis, thus indicating good biocompatibility. In summary, MKPC exhibited good biomechanical properties, high initial strength, good biocompatibility, and low exothermic reaction temperature, demonstrating an excellent application potential in the field of orthopedics.
Author
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.