Zhang, Qing; Qian, Xitang; Thebo, Khalid Hussain; Cheng, Hui-Ming; Ren, Wencai
Science bulletin (Beijing), 06/2018, Volume: 63, Issue: 12Journal Article
Display omitted Tailoring the pore structure and surface chemistry of graphene-based laminates is essentially important for their applications as separation membranes. Usually, pure graphene oxide (GO) and completely reduced GO (rGO) membranes suffer from low water permeance because of the lack of pristine graphitic sp2 domains and very small interlayer spacing, respectively. In this work, we studied the influence of reduction degree on the structure and separation performance of rGO membranes. It was found that weak reduction retains the good dispersion and hydrophilicity of GO nanosheets. More importantly, it increases the number of pristine graphitic sp2 domains in rGO nanosheets while keeping the large interlayer spacing of the GO membranes in most regions at the same time. The resultant membranes show a high water permeance of 56.3 L m−2 h−1 bar−1, which is about 4 times and over 104 times larger than those of the GO and completely reduced rGO membranes, respectively, and high rejection over 95% for various dyes. Furthermore, they show better structure stability and more superior separation performance than GO membranes in acid and alkali environments.
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.