Li, Xiaogang; Nie, Junfeng; Wang, Xin; Li, Kejian; Zhang, Haiquan
Chinese journal of mechanical engineering, 07/2024, Volume: 37, Issue: 1Journal Article
This study analysed the failure of dissimilar metal welds (DMWs) between ferritic heat resistant steels and austenitic stainless steels and investigated its influencing factors by means of numerical simulation, microstructure characterization and mechanical property test. Under the long-term high-temperature service condition in practical power plant, the DMW failure mode was along the interface between nickel-based weld metal (WM) and ferritic heat resistant steel, and the failure mechanism was stress/strain concentration, microstructure degradation and oxidation coupling acting on the interface. The numerical simulation results show that interface stress/strain concentration was due to the differences in coefficient of thermal expansion and creep strength, and the degree of stress/strain concentration was related to service time. The ferrite band formed at the WM/ferritic steel interface was prone to cracking, attracting the fracture along the interface. The interface crack allowed oxidation to develop along the WM/ferritic steel interface. During long-term service, the interface stress/strain concentration, microstructure and oxidation all evolved, which synergistically promoted interface failure of DMW. However, only under the long-term service of low stress conditions could trigger the interface failure of DMW. Meanwhile, long-term service would reduce the mechanical strength and plasticity of DMW.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.