Yang, Jiaoxi; Yu, Xing; Wang, Yanfang; Jia, Wuming; Chen, Hong; Wang, Xibing
Hang kong cai liao xue bao, 06/2018, Volume: 38, Issue: 3Journal Article
To improve the corrosion resistance and load-bearing performance of titanium alloy, the TiC/Ti based composite coating with good metallurgical quality was prepared on the surface of TC4 titanium alloy by using Diode laser, and the effect of TiC content on the microstructures and properties of TiC/TC4 cladding was studied. The microstructure and phase constitution of the coating were characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD), the micro-hardness, corrosion resistance and the load-bearing performance of the coatings were evaluated. The results show that the cladding consists of TiC, TiC0.95, NiTi2 and α'-Ti, and the overall hardness of the coating fluctuates greatly. The micro-hardness in hard phases and in the heat affected zone are 1000-1500HV and about 437HV respectively. While the mass fraction of Ni coated TiC is not higher than 60%, higher corrosion resistance of claddings can be obtained with the increase of the mass fraction of Ni coated TiC, reaching a maximum at 60
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.