DT+ ion irradiation was performed on polycrystalline tungsten, graphite and carbon film and both the amount of retained tritium and the reduction of retained tritium after preservation in vacuum were investigated using an IP technique and BIXS. In addition, the relationship between the retention properties of tritium and the microstructure of graphite and carbon film were studied with Raman spectroscopy. The amount of retained tritium in tungsten was smaller than in both graphite and carbon film. After 1keV of DT+ irradiation, graphite showed no reduction of the amount of retained tritium after six months preservation while that of carbon film decreased by approximately 20% after 40 days preservation. It was suggested that this difference might be associated with differences in the microstructure between graphite and carbon film. In tungsten, the amount of retained tritium decreased to approximately half after 18 days preservation. As the incident energy of implanted tritium to tungsten increased, the decrease in tritium retention during preservation became slower. Tungsten's properties of releasing tritium while preserved in vacuum would be a useful tool for the reduction/removal of retained tritium.