Liu, Yongyue; Xu, Xianglai; Cheng, Jiangxiong; Sun, Hongwei; Ren, Xueping; Jiang, Peng
Materiali in tehnologije, 01/2022, Volume: 56, Issue: 2Journal Article
The hot-deformation behavior of A356 aluminum alloy with a Sr modification was investigated using a Gleeble 1500 thermal simulator. The true stress-strain curves with a deformation temperature of 300–500 °C and a strain rate of 0.01–5 s–1 were clarified. The activation energy of the A356 aluminum alloy with Sr modification was 221.474 kJ/mol. The influences of friction and temperature on the curves were investigated, and then the constitutive equation was established. The results show that the flow stress is obviously affected by temperature and strain rate. The experimental stress is lower than the theoretical stress, and the stress difference between the experimental and theoretical stress increases with the increasing strain. The maximum stress difference reaches 17.8 MPa when the sample deformed at 300 °C/5 s–1 with a reduction of 16 %. For all the deformation conditions the correlation coefficient is 0.99 and the average relative error is 4.8 %, which shows the good predictability of the current model. The developed constitutive equation can provide guidance for the study of the hot-deformation behavior of similar aluminum alloys.
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.