Tong, Y.; Chen, D.; Han, B.; Wang, J.; Feng, R.; Yang, T.; Zhao, C.; Zhao, Y.L.; Guo, W.; Shimizu, Y.; Liu, C.T.; Liaw, P.K.; Inoue, K.; Nagai, Y.; Hu, A.; Kai, J.J.
Acta materialia, 02/2019, Volume: 165, Issue: CJournal Article
A FeCoNiCrTi0.2 high-entropy alloy strengthened by two types of coherent nano-precipitates but with the same composition was fabricated, and its tensile properties at room (293 K) and cryogenic temperatures (77 K) and the corresponding defect-structure evolution were investigated. Compared with the single-phase FeCoNiCr parent alloy, the precipitation-strengthened FeCoNiCrTi0.2 high-entropy alloy exhibits a significant increase in yield strength and ultimate tensile strength but with little sacrifice in ductility. Similar to the single-phase FeCoNiCr high-entropy alloy, the deformation behavior of this precipitation-strengthened FeCoNiCrTi0.2 high-entropy alloy shows strong temperature dependence. When the temperature decreases from 293 K to 77 K, its yield strength and ultimate tensile strength are increased from 700 MPa to 860 MPa and from 1.24 GPa to 1.58 GPa, respectively, associated with a ductility improvement from 36% to 46%. However, different from the single-phase FeCoNiCr high-entropy alloy with a twinning-dominant deformation mode at 77 K, multiple-layered stacking faults with a hierarchical substructure prevail in the precipitation-strengthened FeCoNiCrTi0.2 high-entropy alloy when deformed at 77 K. The mechanism of twinning inhibition in this precipitation-strengthened high-entropy alloy is the high energy barrier for twin nucleation in the ordered γ′ nano-particles. Our results may provide a guide for the design of tough high-entropy alloys for applications at cryogenic temperatures through combining precipitation strengthening and twinning/stacking faults. Display omitted
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.