Xu, Hongmeng; Huang, Haihong
Ceramics international, 08/2022, Volume: 48, Issue: 16Journal Article
The forming quality of thermally sprayed coatings is often severely impacted by inherent defects, including porosity, microcracks, and mechanical bonding. The poor adhesive strength hinders the utilization of thermal spray technology when fabricating ceramic-reinforced metal matrix composite coatings (MMCCs). Thus, in this study, a negative defocus laser remelting and injection method (LRI) is introduced to modify a thermally sprayed coating with WC ceramics. The microstructure and mechanical property (microhardness, elastic modulus, and wear resistance) evolution of a LRI-modified WC reinforced composite coating is systematically characterized and compared with that for an as-sprayed coating. The LRI method is proven to improve the inherent defects of the initial coating and avoid severe reactions and dissolution of reinforced particles at high temperatures, and can be used to form a high-quality composite coating with a maximum strengthening effect of the ceramic particles. Compared with the initial coating, the elastic modulus and microhardness of the LRI coating are increased by 57.22% and 111.06%, respectively, whereas the abrasion rate is decreased by 54.33%.
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.