Zhang, Lingyan; Peng, Ching-Tun; Guan, Jintong; Lv, Peng; Guan, Qingfeng; Lu, Ruifeng
Nanomaterials (Basel, Switzerland), 01/2019, Volume: 9, Issue: 1Journal Article
In this investigation, chromium (Cr) was adopted as an alloying element on a nickel substrate, and the alloying process was materialized via high-current pulsed electron beam (HCPEB) irradiation. X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were also conducted for microstructure characterization. The results showed that after HCPEB irradiation a nanocrystalline Cr-Ni alloying layer was formed and numerous dislocations were generated, resulting in a great deal of diffusion paths for Cr elements. Moreover, properties including hardness, wear and electrochemical performance were significantly improved after HCPEB irradiation, which was mainly due to the formation of the nanocrystalline Cr⁻Ni alloying layer. In addition, each strengthening mechanism that contributed to the hardness of the HCPEB-irradiated sample was mathematically analyzed, and solid solution strengthening was found to be of great importance.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.