Stevenson, Ryan; Toumpis, Athanasios; Galloway, Alexander
Materials & design, 12/2015, Volume: 87Journal Article
Friction stir welding of steel is in the early stages of development. The aim to commercialise this process creates a trade-off between welding time, cost and quality of the joint produced. Therefore, it becomes critical to analyse the lower quality bound of steel friction stir welds in conventional square edge butt welding configuration. Work has been undertaken to evaluate the microstructure and fatigue performance of 6mm thick DH36 steel plates friction stir welded with sub-optimal process conditions, resulting in the development of embedded and surface breaking flaws. The defective weldments were characterised to understand the nature of the flaws and a programme of mechanical testing was undertaken (including fatigue assessment) to determine the relationship between the flaw geometry, location and weld quality. A number of characteristic flaws were identified and seen to interact with the samples' fatigue fracture mechanisms. Samples with wormholes at the weld root produced the lowest fatigue performance. Fracture from incomplete fusion paths at the retreating side of the welds' top surface was seen to correspond to the highest recorded fatigue lives. The work provides an insight into the complex nature of characteristic flaws in steel friction stir welds and their interaction with fatigue behaviour. Display omitted •Ductile failure in PM during tensile testing did not indicate inherent flaws.•Fatigue performance of FSW of DH36 was influenced by characteristic flaws.•The highest fatigue results corresponded to fracture at incomplete fusion paths.•Longitudinal fatigue tests fractured from top surface incomplete fusion paths•Tensile residual stresses reduced longitudinal fatigue lives.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.