Dong, Qi; Li, Haolin; Xing, Shuming; Qiu, Bo
Materials, 08/2022, Volume: 15, Issue: 16Journal Article
Al-Ti-C master alloy agent is currently the most promising grain refiner. This work investigates the influence of Tisub.3AlCsub.2 addition (1.0-3.0 wt.%) on the microstructure of a hypoeutectic cast iron (4.7 wt.% Cr, 2.3 wt.% C). Microstructures of the samples were examined by SEM (scanning electron microscope). It was demonstrated that the added Tisub.3AlCsub.2 did reduce the size of coarse primary carbides. The XRD (X-ray diffraction) pattern shows that Tisub.3AlCsub.2 is decomposed into TiC in the alloy substrate. The EDS (energy dispersive spectrometer) interfacial element analysis shows that TiC combines well with the matrix interface. As the Tisub.3AlCsub.2 amount was increased, the finest microstructure was achieved. When 2 wt.% Tisub.3AlCsub.2 was added, the wear-resistance property of the material improved and became two times harder than the former. However, when 3% Tisub.3AlCsub.2 was added, TiC gathered at the crystal boundary, which caused a decrease in the wear resistance of the material.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.