  • The role of cerium valence in the conversion temperature of ▫$H_2$▫ ▫$Ti_3O_7$▫ nanoribbons to ▫$TiO_2$▫-B and anatase nanoribbons, and further to rutile
    Umek, Polona ...
    CeO2 -TiO2 is an important mixed oxide due to its catalytic properties, particularly in heterogeneous photocatalysis. This study presents a straightforward method to obtain 1D TiO2 nanostructures ... decorated with CeO2 nanoparticles at the surface. As the precursor, we used H2Ti3O7 nanoribbons prepared from sodium titanate nanoribbons by ion exchange. Two cerium sources with an oxidation state of +3 and +4 were used to obtain mixed oxides. HAADF–STEM mapping of the Ce4+-modified nanoribbons revealed a thin continuous layer at the surface of the H2Ti3O7 nanoribbons, while Ce3+ cerium ions intercalated partially between the titanate layers. The phase composition and morphology changes were monitored during calcination between 620 ◦C and 960 ◦C. Thermal treatment led to the formation of CeO2 nanoparticles on the surface of the TiO2 nanoribbons, whose size increased with the calcination temperature. The use of Ce4+ raised the temperature required for converting H2Ti3O7 to TiO2 -B by approximately 200 ◦C, and the temperature for the formation of anatase. For the Ce3+ batch, the presence of cerium inhibited the conversion to rutile. Analysis of cerium oxidation states revealed the existence of both +4 and +3 in all calcined samples, regardless of the initial cerium oxidation state.
    Vir: Molecules [Elektronski vir]. - ISSN 1420-3049 (Vol. 28, 15, 2023, str. 1-14)
    Vrsta gradiva - e-članek ; neleposlovje za odrasle
    Leto - 2023
    Jezik - angleški
    COBISS.SI-ID - 160531203

    Povezava(-e):

    https://www.mdpi.com/1420-3049/28/15/5838
    DOI

Vnos na polico