Comparison of ECN measurements and analysis during the SCC processes on stainless steel under different mechanical conditionsBajt Leban, Mirjam ...Electrochemical noise measurements have been performed on electrodes made from the same piece of stainless steel, of type AISI 304. Potential and current noise were measured under open circuit ... conditions in a three-electrode system, where one of the electrodes was kept under the load and acted as a common working electrode. Two types of electrode set-ups were used, differing in the method of load application. In the first case the common electrode was in the shape of a U-bend (under a static, undefined load), whereas in the second case the common electrode was subjected to a constant, slowly increasing stress (the SSRT test). The first type of test was performed in a concentrated magnesium chloride solution at an elevated temperature. In order to detect the time when cracks initiated, the probes were dismantled daily, and examined visually using an optical microscope. SSRT tests were performed in diluted sodium thiocyanate solution with or without additions of chlorides. Electrochemical voltage and current noise and changes of stress and elongation were measured simultaneously. During the latter part of both types of tests, significant simultaneous spikes of voltage and current noise were observed. The spikes detected during the SSRT test were correlated with drops in stress and sudden increases in elongation. After the measurements had been performed, several characteristic time series (cracking non-active and cracking active) were subjected to spectral and chaos analysis. So far, analysis of such non-stationary signals, in particular of electrochemical systems (a U-bend exposed to a concentrated magnesium chloride solution) during uniform corrosion, cannot yet provide any satisfactory explanation of the comlpex mechanisms of stress-corrosion cracking processesVir: Corrosion 99 : 54th annual conferenece and exposition, April 25-30, 1999, San Antonio, Texas : CORROSION NACExpo (Paper No 202 (7 str.))Vrsta gradiva - prispevek na konferenciLeto - 1999Jezik - angleškiCOBISS.SI-ID - 241255
Avtor
Bajt Leban, Mirjam |
Doleček, Valter |
Legat, Andraž |
Kuhar, Viljem
Teme
SSRT tests |
electrochemical noise |
austenitic stainless steel |
stress-corrosion cracking |
sensitization |
U-bend specimens |
current and potential transients |
spectral and chaos analysis |
občutljivost na napetostno-korozijsko pokanje |
elektrokemijski šum |
tokovni in napetostni dogodki |
elektrokemija |
spektralna analiza |
napetostno-korozijsko pokanje |
kaotična analiza |
materiali |
U-preskušanci |
korozija |
avstenitno nerjavno jeklo
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Bajt Leban, Mirjam | 16394 |
Doleček, Valter | 00869 |
Legat, Andraž | 08281 |
Kuhar, Viljem | 17353 |
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Obvestilo
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Mesto prevzema | Status gradiva | Rezervacija |
---|
Prosimo, počakajte trenutek.