Analysis of cracking of co-extruded recovery boiler floor tubesKeiser, James R. ...Cracking of stainless steel layer in co-extruded 304L/SA210 tubing used in black liquor recovery boilers is being found in an ever-increasing number of North American pulp and paper mills. Studies ... are being conducted to determine the cause of the cracking and to identify alternate materials and/or operating procedures to prevent tube cracking. Examination of cracked tubes has permitted characterization of crack features, and transmission electron microscopy is providing information about the thermal history, particularly cyclic thermal exposures, that tubes have experienced. Neutron and X-ray diffraction techniques are being used to determine the residual stresses in as-fabricated tube panels and exposed tubes, and finite element modeling is providing information about the stresses the tubes experience during operation. Laboratory studies are being conducted to determine the susceptibility of the co-extruded 304L/SA210 tubes to stress corrosion cracking, thermal fatigue, and corrosion in molten smelt. On the basis of all these studies, recommendations for means to prevent tube cracking will be offered.Vir: Engineering & papermakers : forming bonds for better papermaking. Book 3 : october 6-9, 1997, Opryland Hotel, Nashville, TN (Str. 1025-1041)Vrsta gradiva - prispevek na konferenciLeto - 1997Jezik - angleškiCOBISS.SI-ID - 395201
Avtor
Keiser, James R. |
Taljat, Boštjan |
Wang, Xun-Li |
Swindeman, Robert W. |
Maziasz, Philip J. |
Thomas, Richard L. |
Payzant, E. A. |
Singbeil, Douglas L. |
Prescott, Robert
Teme
cevi |
grelci |
pokanje |
preostale napetosti |
tubes |
boilers |
cracking |
residual stresses
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Taljat, Boštjan | 11700 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: