Study of oxide protective layers on stainless steel by AES, EDS and XPSMandrino, Djordje, 1964-2021 ...A protective oxide layer was formed on the surface of stainless steel by standard industrial-type thermal treatment. Additional post-thermal treatment annealing and polishing followed by annealing ... were applied in an attempt to improve characteristics of the layers. Oxide layers formed on samples without and with different types of post-thermal treatment processing were analysed and compared. Several techniques were employed. SEM was used to image the surface; AES, CPS and energy-dispersive spectroscopy (EDS) were all used to probe the elemental composition of the oxide layers. AES was also used as the most straight forward method to obtain depth profiles. Low beam energy EDS was used in an attempt to obtain some fast averaged volume information from the layers. XPS was mainly used for determining chemical states on the surface of the sample but not for depth profiling (low sputtering rate due to large illuminated area). Analysed samples differed with regard to surface morphology of the oxide layers, oxide layer compositions and thicknesses. An attempt was made to relate these differences to differences in post-thermal treatment procedures.Vir: The 12th European conference on applications of surface and interface analysis : Brussels, Belgium, 9-14 September 2007 : ECASIA`07 (Vol. 40, no. 3-4, 2008, str. 285-289)Vrsta gradiva - prispevek na konferenciLeto - 2008Jezik - angleškiCOBISS.SI-ID - 671402
Avtor
Mandrino, Djordje, 1964-2021 |
Godec, Matjaž, 1961- |
Torkar, Matjaž |
Jenko, Monika, metalurginja
Teme
AES |
EDS |
XPS |
oxide layer |
stainless steel |
AES |
EDS |
XPS |
oksidna plast |
nerjavno jeklo
![loading ... loading ...](themes/default/img/ajax-loading.gif)
vir: The 12th European conference on applications of surface and interface analysis : Brussels, Belgium, 9-14 September 2007 : ECASIA`07 (Vol. 40, no. 3-4, 2008, str. 285-289)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Mandrino, Djordje, 1964-2021 | 08850 |
Godec, Matjaž, 1961- | 10842 |
Torkar, Matjaž | 05438 |
Jenko, Monika, metalurginja | 05675 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: