Analysis of crack formation on a single part glass mouldTehovnik, Franc ...The analysis of the formation of longitudinal crack, which appeared on a single part glass mould, is presented in the work. The mould was made from AISI 314 steel, a temperature resistant stainless ... steel. The depth of the longitudinal cracks was approximately 3 mm. The cracks were divided into microcracks at the tip. Chromium and iron oxides were identified as was the presence of both sulphur and calcium. The crack had expanded transcrystalline due to stress corrosion. The fracture surface was gained by propagating existing cracks and shows a transcrystalline fracture due to hydrogen embrittlement. Atomic hydrogen, a product of corrosion, dissolves itself in the austenitic steel matrix at higher temperatures. The effect of hydrogen is so potent that it causes a brittle fracture in steel that is tough even at low temperatures. This kind of corrosion can cause transcrystalline cracks at only 50 % of the yield strength, the cracks are also affected by internal stresses. Even small stresses can cause the formation and advancement of stress corrosion.Vir: Program in knjiga povzetkov = Program and book of abstracts (Str. 221)Vrsta gradiva - prispevek na konferenciLeto - 2012Jezik - angleškiCOBISS.SI-ID - 969642
Avtor
Tehovnik, Franc |
Torkar, Matjaž |
Arzenšek, Boris |
Žužek, Borut |
Burja, Jaka |
Medvešek, Srečko
Teme
AISI 314 steel |
glass mould |
crack formation |
analysis
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Tehovnik, Franc | 08001 |
Torkar, Matjaž | 05438 |
Arzenšek, Boris | 08236 |
Žužek, Borut | 32177 |
Burja, Jaka | 35645 |
Medvešek, Srečko | ![]() |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: