Wear mechanisms in oil-lubricated and dry fretting of silicon nitride against bearing steel contactsKalin, Mitjan ...ǂThe ǂwear and friction behaviour of silicon nitride against bearing steel was investigated under lubricated and dry fretting conditions as a function of amplitude and test duration. Tests were ... performed on a high frequency fretting tester. Silicon nitride bearing balls were used as the upper oscillating specimens while the lower stationary flats were standard specimens of bearing steel. Amplitudes in the intermediate 5 to 50 *m range and a test duration from 10 to 360 minutes were studied. In lubricated conditions a commercial lubricant, ISO VG 220, was used. Light microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), Auger spectroscopy (AES) and transmission electron microscopy (TEM) were employed to determine the wear mechanisms. Under lubricated conditions transition from high to low wear volumes was recognised with increasing amplitude. At lower amplitudes and in the early stage of fretting tests at moderate amplitudes, mechanical wear dominated. Cracks on the stick-slip boundary and spalling of a thin tribolayer was observed. Under these conditions the highest wear in lubricated fretting was obtained. In the final stage of fretting tests at moderate amplitudes, and from the beginning at higher amplitudes, tribochemical wear is suggested as the dominant wear form. A 0.2 mm thick tribolayer was observed on the contact, containing inclusions with different Fe and Si contents. A very high concentration of carbon, formed by oil degradation, was also determined in this layer, confirming the critical influence of oil on the wear behaviour. Quite a different wear mechanism is proposed for dry fretting conditions. Results of AES analyses showed an order of magnitude thicker layer than in lubricated fretting, also having a remarkably different chemical composition. TEM analysis confirmed that the reaction layer consists of a silica-rich amorphous phase containing small inclusions of Fe2O3 and Fe3O4. In contrast to lubricated conditions, where the layer created was ductile, in the case of dry fretting the layer was brittle. The continuous process of forming and spalling the brittle tribolayer caused much higher wear rates and wear losses than under lubricated fretting conditions. No transition in wear behaviour was observed as was the case in lubricated fretting.Vir: Wear of materials : proceedings of the Eleventh International Conference on Wear Materials, San Diego, California, April 20-23, 1997 (12 str.)Vrsta gradiva - prispevek na konferenciLeto - 1997Jezik - angleškiCOBISS.SI-ID - 3025691
Avtor
Kalin, Mitjan |
Vižintin, Jože |
Novak, Saša |
Dražić, Goran
Teme
tribologija |
odrezavanje |
obraba materialov |
mehanizmi obrabe |
jeklo ležajno |
keramika |
Si3N4 |
metode eksperimentalne |
mazanje |
pogoji obdelav |
obdelave mokre |
obdelave suhe |
olja |
fretting wear |
silicon nitride |
bearing steel |
ceramics |
oil |
lubricated conditions |
dry conditions
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Kalin, Mitjan | 14556 |
Vižintin, Jože | 00812 |
Novak, Saša | 04292 |
Dražić, Goran | 02556 |
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Obvestilo
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Mesto prevzema | Status gradiva | Rezervacija |
---|
Prosimo, počakajte trenutek.