The aim of the study was to evaluate the performance of tannin mordant from Psidium guajava leaves, Peltophorum pterocarpum bark, and Coffea arabica leaves in cotton batik dyeing using tingi bark ...(Ceriops tagal). This research was conducted by initial quantitative analysis of each extract to measure the quantity of tannin using UV-Vis spectrophotometry with tannic acid as a standard solution. The next process was a fabric pre-mordanting using each mordant extract, batik process, coloring with tingi bark extract, and post-mordanting using each alum solution and guava leaves extract. The dyed batik fabric was tested toward its color intensity and durability/fastness properties. From the quantitative analysis, guava leaves extract contains the biggest tannin content compared with jambal bark and coffee leaves extract, which is 1151.5 μg/mL. The dyed sample from combination of Guava leaves extract pre-mordanting with alum post-mordanting provided the best color intensity of 15.52. While all variables had an equal good value for washing fastness. It can be concluded that all material had potential as natural mordant for cotton batik dyeing with natural dye, but with consideration of using metal mordant for combination to get better results in terms of both color intensity and fastness properties.Keywords: batik; biomordant; natural dye; tannin mordant A B S T R A KTujuan dari penelitian ini adalah untuk mengetahui kinerja mordan tanin dari daun jambu biji (Psidium guajava), kulit kayu jambal (Peltophorum pterocarpum) dan daun kopi (Coffea arabica) dalam pewarnaan kain batik katun dengan pewarna alami tingi (Ceriops tagal). Penelitian dilakukan dengan terlebih dahulu mengukur kadar tanin total dari masing-masing ekstrak secara kuantitatif menggunakan spektrofotometri UV-Vis dengan larutan standar asam tanat. Proses selanjutnya adalah mordan awal kain menggunakan masing-masing ekstrak mordan, pembatikan, pewarnaan menggunakan ekstrak kulit kayu tingi, dan mordan akhir menggunakan masing-masing larutan tawas dan ekstrak daun jambu biji. Kain batik berwarna diuji ketuaan warna dan ketahanan luntur warnanya. Dari hasil analisis kuantitatif, didapatkan kandungan tanin terbesar dari ekstrak daun jambu biji yaitu 1.151,5 μg/mL. Hasil uji ketuaan warna paling besar didapatkan dari perlakuan mordan awal daun jambu biji dan mordan akhir tawas dengan nilai 15,52, sedangkan ketahanan luntur warna terhadap pencucian secara rata-rata memberikan nilai 4 (baik) untuk semua variabel. Kesimpulan yang dapat diambil yaitu ekstrak daun jambu biji, kulit kayu jambal, dan daun kopi memiliki potensi untuk digunakan sebagai bahan mordan pada pewarnaan batik. Penggunaan ketiga bahan mordan alami memerlukan kehadiran mordan logam untuk memperkuat intensitas warna dan ketahanan luntur warna kain.Kata kunci: batik; biomordan; mordan tannin; pewarna alam
Indonesia coal ash is predicted to reach 10.8 million tons in the year 2020 but its utilization is still limited. In the last decade, coal ash has become a promising REY source candidate. To ...determine the potency of REY in Indonesia coal ash, information about element concentration and mineralogy of the ash is essential. In this study, coal ash samples were taken from Paiton-2, Pacitan, Rembang, and Tanjung Jati coal-fired power plants. Element content and mineralogy were analyzed using Inductive Couple Plasma Mass Spectroscopy/Atomic Emission Spectroscopy (ICP-MS/AES), X-Ray Diffractometer (XRD) and petrographic. The results showed that coal fly ash and bottom ash contains critical REY in the range of 38% to 41% with Coutlook larger than one. XRD analysis showed that both fly ash and bottom ash have similar mineral phases with slightly different concentrations. The mineral phase is dominated by amorphous glass, quartz, Fe-bearing minerals, and unburned carbon. The amorphous glass phase in fly ash is in the range of 23 to 34% while in bottom ash between 14 and 34%. Unburned carbon content in fly ash and bottom ashes are 7-13% and 7-19%, respectively. Fe-bearing mineral content in fly ash is 15-20% and bottom ash is 13-20%. In addition, Indonesia coal ash has a higher Heavy-REY enrichment factor than Light-REY. The Enrichment Factor of HREY in fly ash is as much as 1.3 times (in average) of the bottom ash.
The natural dye extracted from Swietenia mahagoni was applied to silk batik. Mahagoni bark is known to contain dyestuff components such as flavonoids and tannins. The dye compound was extracted using ...water at pH values of 6 (original pH extract), pH 2 (acid), and pH 12 (base) at 100 °C for 1 hour. Variation of extraction pH values was carried out to determine the influence of temperature on the results of the extract. Batik dyeing was carried out at room temperature using dye products. The pre-mordanting and post-mordanting used were alum (Al2(SO4)3.K2SO4.24H2O). The results showed that the dye product extracted in alkaline pH shows a high amount of tannins and flavonoids and the ability to color the silk batik better. The color direction is reddish-brown. The pH values of extraction do not affect the results of the colorfastness to washing test, which is on 4-5 (good) scale. A B S T R A KPewarna alami yang diekstrak dari mahoni (Swietenia mahagoni) diaplikasikan pada kain batik sutra. Kulit kayu mahoni diketahui mengandung komponen zat warna berupa flavonoid dan tanin. Komponen zat warna diekstraksi menggunakan air pada pH 6, pH 2 (asam) dan pH 12 (basa) pada suhu 100 °C selama 1 jam. Variasi pH ekstraksi dilakukan untuk mengetahui pengaruhnya terhadap hasil ekstrak. Pewarnaan dilakukan pada suhu ruang menggunakan pewarna hasil ekstraksi. Mordan awal dan mordan akhir yang digunakan adalah tawas (Al2(SO4)3.K2SO4.24H2O). Ekstraksi pada pH basa terbukti meningkatkan jumlah zat tanin dan flavonoid yang terekstrak dan mampu mewarnai kain batik sutra dengan lebih baik. Arah warna yang dihasilkan adalah cokelat kemerahan. Derajat keasaman (pH) ekstraksi tidak berpengaruh pada hasil uji ketahanan luntur warna terhadap pencucian, yaitu skala 4-5 (baik).
ZnO nanoparticle was synthesized by a simple hydrometallurgical method using raw material of electric arc furnace dust (EAFD),which is a solid waste in the stainless steel industry. Electric arc ...furnace dust contains 68.81% Zn in the form of zincite (ZnO) and simonkolleite (H10Cl2O9Zn5). The synthesis was carried out in two main steps, i.e., leaching and alkaline precipitation. In this study, the effect of leaching reagent, leaching temperature, and leaching reagent concentration on the percent extraction of Zn in the leaching process from electric arc furnace dust and the characteristics of the resulting ZnO product were studied. The experimental results showed that leaching reagent of acetic acid gives the highest percent extraction of Zn. The results also showed that the increase of temperature and acid concentration could improve the Zn extraction percentage. At 2M acid concentration, Zn extraction percentage already achieved 100%; hence the process is independent of temperature. The ZnO product has a purity of 96%. The XRD data confirmed the nano sizes of the ZnO product. A B S T R A KZnO nanopartikel disintesis dengan metode hidrometalurgi sederhana menggunakan bahan baku berupa debu tungku busur listrik yang merupakan limbah padat industri baja tahan karat. Debu busur listrik mengandung 68,81% Zn dalam bentuk zincite (ZnO) dan simonkolleite (H10Cl2O9Zn5). Proses sintesis dilakukan dalam dua tahap utama yaitu pelindian dan pengendapan alkali. Pada penelitian ini dipelajari pengaruh reagen pelindian, suhu pelindian, dan konsentrasi reagen pelindian pada proses pelindian terhadap persen ekstraksi Zn dari debu tungku busur listrik dan karakteristik produk ZnO yang dihasilkan. Hasil percobaan menunjukkan bahwa asam asetat adalah reagen pelindian yang memberikan persen ekstraksi Zn tertinggi. Hasil percobaan juga menunjukkan bahwa semakin tinggi suhu dan konsentrasi asam yang digunakan, maka semakin meningkat persen ekstraksi Zn yang diperoleh. Tetapi pada konsentrasi asam 2M, suhu pelindian tidak terlalu berpengaruh karena dengan konsentrasi asam asetat 2M pada semua kondisi suhu pelindian, persen ekstraksi Zn yang diperoleh adalah 100%. Hasil pelindian menggunakan asam asetat pada kondisi optimum menghasilkan produk ZnO dengan kemurnian sekitar 96%. Data XRD juga menunjukkan bahwa ZnO yang terbentuk memiliki ukuran nano.
Batik is an Indonesian traditional cloth which has been recognised as an Intangible Cultural Heritage of Humanity by UNESCO for more than a decade. Batik cloth is popular among Indonesian people for ...daily use, both for formal and informal occasions. Commonly, batik cloth is made from cotton, which has many advantages, however prone to bacterial growth, particularly in the tropical climate. Therefore, it is important to develop batik cloth with antibacterial properties. The antibacterial properties of batik cloth were achieved by applying ZnO nanoparticles as antibacterial agent. The nanoparticles were synthesised using precipitation-sonication method. The formed ZnO nanoparticles were in an average particle size of 54.76 nm and 99.77% ZnO content. The batik making process utilized a synthetic reactive dye of remazol-turquoise blue. The effect of process sequence, the level of antibacterial properties, the morphology of the ZnO coated fabric, and the effect of the application of nanoparticle on the dyeing process were investigated. The results showed that ZnO nanoparticle application on the batik fabric led to antibacterial properties. The process sequences in adding the ZnO nanoparticles were confirmed to significantly affect the antibacterial effectivity and the colour strength. The application of ZnO nanoparticles did not affect the colour fastness to washing as the test showed similar value to that of without ZnO treatment. In addition, the application of ZnO nanoparticles affects the mechanical properties by increasing the tensile strength and decreasing the elongation at break. The application of ZnO after batik making process was shown to have a greater effect on the mechanical properties.
Tujuan dari penelitian ini adalah untuk menilai kemungkinan penggunaan bentonit sebagai mordan potensial dalam pewarnaan alam pada kain batik katun dengan kayu secang (Caesalpinia Sappan Linn.). ...Karakterisasi bentonit dilakukan dengan menggunakan Spektrometer Infra Merah dan analisis banyaknya Al yang terkadung dalam bentonit alam dilakukan dengan menggunakan Spektrofotometer Serapan Atom (AAS). Proses mordan kain katun dilakukan dengan perbandingan berat kain:air 1:50. Variasi banyaknya bentonit yang digunakan yaitu 3%, 6%, dan 9% dari berat kain. Proses mordan dilakukan pada suhu 90 °C selama 45 menit dan dibiarkan selama 12 jam pada suhu kamar. Pewarnaan dilakukan dengan menggunakan ekstrak ZWA Kayu Secang hasil dari proses ekstraksi zat warna alam pada suhu 100 °C selama 60 menit. Hasil spektra IR memberikan informasi tentang keberadaan unit pembangun tetrahedral dalam kerangka bentonite serta interaksi ikatannya. Pita serapan khas untuk struktur bentonit diperoleh pada bilangan gelombang 794 cm¬-1, 470 cm¬-1 dan 1056 cm¬-1. Jumlah kandungan Al dalam sampel bentonit alam adalah 6,81%. Hasil pewarnaan sampel menggunakan ekstrak zat warna alam secang dengan mordan akhir bentonite memiliki arah warna merah kecoklatan dengan nilai ketuaan warna -36,38 pada sampel batik dengan mordan bentonit 3% adalah dan 36,76 pada sampel batik dengan mordan bentonit 9%. Keduanya memiliki nilai ketuaan warna yang hampir sama dengan sampel pewarnaan batik menggunakan mordan tawas yaitu sebesar -37,48. Hasil uji ketahanan luntur warna kain terhadap pencucian sampel pewarnaan menggunakan mordan bentonit memiliki nilai 4 (baik) untuk maksimum penggunaan 6% dan 3-4 (cukup baik) untuk sampel pewarnaan menggunakan mordan bentonite 9%. Berdasarkan hasil uji dan analisa yang dilakuklan, bentonit berpotensi untuk digunakan sebagai mordan dalam pewarnaan alam pada kain batik katun dengan kayu secang (Caesalpinia Sappan Linn.). Kata Kunci: batik, batik warna alam, secang, bentonit, mordan alam
Penelitian bertujuan mengidentifikasi masalah Pendidikan Anak Usia Dini berdasarkan persepsi guru di Kota Medan. Metode penelitian yang digunakan adalah survei melibatkan 20 responden guru PAUD di ...Kota Medan. Teknik pengumpulan data dilakukan dengan angket dan dianalisis menggunakan statistik deskriptif. Hasil penelitian menunjukkan bahwa urutan masalah PAUD secara umummasalah kesejahteraan guru, animo masyarakat yang kurang dan pendampingan pemerintah kurang, kualtas pengelolaan PAUD, kebijakan pemerintah belum komprehensif, kualitas guru kurang memadai, Kesadaran masyarakat yang kurang, jumlah sekolah belum cukup. Masalah pembelajaran PAUD dengan urutan prioritas media pembelajaran yang terbatas, partisipasi orang tua rendah, kemampuan guru mengelola kelas masih kurang, jumlah peserta didik yang terlalu banyak di kelas, perkembangan anak yang lambat, lingkungan yang tidak kondusif, kurangnya jumlah guru di kelas, fasilitas pembelajaran yang kurang memadai. Kesimpulan penelitian ini adalah masalah pendidikan PAUD secara umum adalah kesejahteraan guru dan masalah utama pendidikan PAUD dalam pembelajaran adalah media pembelajaran yang terbatas.
Telah dilakukan penelitian pemanfaatan kulit kayu angsana (Pterocarpus indicus) sebagai sumber zat warna alam untuk pewarnaan kain batik sutera. Ekstraksi ZWA dilakukan dengan pelarut air dengan ...variasi suhu ekstraksi 75 °C dan 100 °C. Pewarnaan zat warna alam kemudian diaplikasikan pada kain batik sutera pada kondisi pencelupan asam (pH 4) dan basa (pH 10). Mordan awal yang digunakan adalah tawas dan jirak. Diakhir pewarnaan alam dilakukan fiksasi dengan menggunakan tawas dan tunjung. Berdasar hasil penelitian, kulit kayu angsana terbukti dapat digunakan sebagai sumber zat warna alam untuk batik sutera. Ketuaan warna paling tinggi diperoleh pada pewarnaan batik sutera dengan menggunakan mordan jirek pada suhu ekstraksi 100 °C dalam kondisi pencelupan basa dengan fiksator tunjung. Arah warna yang dihasilkan adalah coklat tua pada suasana pencelupan asam dengan fiksasi tunjung, coklat kemerahan pada suasana pencelupan asam fiksasi tawas, coklat kemerahan pada suasana pencelupan basa fiksasi tawas dan coklat tanah pada suasana pencelupan basa dengan fiksasi tunjung. Hasil uji ketahanan luntur warna terhadap pencucian dari sampel pewarnaan menunjukkan kualitas baik yaitu pada skala 4-5 (Baik). Study on utilizationof angsana (Pterocarpus indicus) as natural dye for silk batik has been conducted. The study was aimed to determine the quality of the natural dyeing of the bark of angsana by use jirak (Symplocos fasciculata Zoll.) and alum as the natural mordant. Extraction of natural dye was carried out using water by varying the extraction temperature of 75 and 100 °C. The coloration was applied to silk batik at both acid (pH 4) and basic (pH 6) impregnations. The mordant employed were alum and jirak. The last stage was fixation using alum and ferrosulfate. Based on the results, angsana was proved to be used as a source of natural dyes for silk batik. The highest color intensity was obtained by using angsana bark extract and jirak as mordant at 100 °C under basic condition the presence of ferrosulfate as the fixative. The obtained color shades for acid impregnation with ferrosulfate fixative, acid impegnation with alum fixative, basic impregnation with alum fixative and basic impregnation with ferrosulfate fixative, were dark brown, reddish brown, reddish brown and soil brown, respectively. The test of fastness to washing towards coloration sample gave good quality on scale of 4-5 (good).
PDF