Aim of this in vitro study was to analyze structural properties of two different polymeric orthodontic aligners, Exceed30 (EX30) and Smart Track (LD30), before and after use. Forty patterns of ...aligners were randomly selected: 20 LD30 and 20 EX30, worn intra-orally for 14±3 days, 22 h/day. From each aligner, 10 specimens were prepared from buccal surfaces of the incisor region by the cutting of samples 5×5 mm under a stereomicroscope. All samples were subjected to Fourier transform infrared spectroscopy, micro-Raman spectroscopy, X-ray diffraction, tensile and indentation strength test. LD30 appeared more homogeneous, with a crystalline fraction lower than EX30 and exhibited a higher elastic behavior and a lower tendency to warp after use than EX30. LD30 demonstrated better adaptability to the dental arch and greater consistency of application of orthodontic forces than produced with EX30. However, both materials showed structural modifications that resulted in increased sample hardness and hyper-plasticity.
Electrocorticography (ECoG) is becoming a common tool for clinical applications, such as preparing patients for epilepsy surgery or localizing tumor boundaries, as it successfully balances ...invasiveness and information quality. Clinical ECoG arrays use millimeter-scale electrodes and centimeter-scale pitch and cannot precisely map neural activity. Higher-resolution electrodes are of interest for both current clinical applications, providing access to more precise neural activity localization and novel applications, such as neural prosthetics, where current information density and spatial resolution is insufficient to suitably decode signals for a chronic brain-machine interface. Developing such electrodes is not trivial because their small contact area increases the electrode impedance, which seriously affects the signal-to-noise ratio, and adhering such an electrode to the brain surface becomes critical. The most straightforward approach requires increasing the array conformability with flexible substrates while improving the electrode performance using materials with superior electrochemical properties. In this paper, we propose an ultra-flexible and conformable polyimide-based micro-ECoG array of submillimeter recording sites electrochemically coated with high surface area conductive polymer-carbon nanotube composites to improve their brain-electrical coupling capabilities. We characterized our devices both electrochemically and by recording from rat somatosensory cortex in vivo. The performance of the coated and uncoated electrodes was directly compared by simultaneously recording the same neuronal activity during multiwhisker deflection stimulation. Finally, we assessed the effect of electrode size on the extraction of somatosensory evoked potentials and found that in contrast to the normal high-impedance microelectrodes, the recording capabilities of our low-impedance microelectrodes improved upon reducing their size from 0.2 to 0.1 mm.
In this paper, we present an ultraflexible tactile sensor, in a piezo-eletricoxide-semiconductor FET configuration, composed by a polyvinylidenefluoride-co-trifluoroethylene capacitor with an ...embedded readout circuitry, based on nMOS polysilicon electronics, integrated directly on polyimide. The ultraflexible device is designed according to an extended gate configuration. The sensor exhibits enhanced piezoelectric properties, thanks to the optimization of the poling procedure (with electric field up to 3 MV/cm), reaching a final piezoelectric coefficient d 33 of 47 pC/N. The device has been electromechanically tested by applying perpendicular forces with a minishaker. The tactile sensor, biased in a common-source arrangement, shows a linear response to increasing sinusoidal stimuli (up to 2 N) and increasing operating frequencies (up to 1200 Hz), obtaining a response up to 430 mV/N at 200 Hz for the sensor with the highest value of d 33 . The sensor performances were also tested after several cycles of controlled bending in different amount of humidity with the intent to investigate the device behavior in real conditions.
Bacterial adhesion to the surface of orthodontic materials is an important step in the formation and proliferation of plaque bacteria, which is responsible for enamel demineralization and ...periodontium pathologies. With the intent of investigating if adhesive resins used for bracket bonding are prone to bacteria colonization, the surface roughness of these materials has been analyzed, combining information with a novel methodology to observe the internal structures of orthodontic composites. Scanning electron microscopy, combined with focus ion bean micromachining and stylus profilometry analyses, were performed to evaluate the compositional factors that can influence specific pivotal properties facilitating the adhesion of bacteria to the surface, such as surface roughness and robustness of three orthodontic adhesive composite resins. To confirm these findings, contact angle measurements and bacteria incubation on resin slide have been performed, evaluating similarities and differences in the final achievement. In particular, the morphological features that determine an increase in the resins surface wettability and influence the bacterial adhesion are the subject of speculation. Finally, the focused ion beam technique has been proposed as a valuable tool to combine information coming from surface roughness with specific the internal structures of the polymers.
Fluoride-based mouthwashes and gels are preventive measures in countering demineralization and caries but, modifying environmental acidity, can reduce the wet corrosion resistance of orthodontic ...alloys. To evaluate chemical stability, in vitro experiments were conducted on stainless steel and nickel–titanium wires, weighed before and after immersion in household fluorinated mouthwashes and gels, measuring weight variations and elution of metal ions from acid corrosion phenomena. Elution samples were analyzed by inductively coupled plasma mass spectrometry, detecting residual ion concentration, while surface changes were analyzed under scanning electron microscopy. Results showed stainless steel wires do not undergo significant erosion when exposed to most fluorinated mouthwashes but, at prolonged exposure, alloys elute gradually greater amounts of metals and Ni–Ti wires become more sensitive to some mouthwashes. Ions’ elution varies considerably, especially for Ni–Ti wires, if exposed to household fluorinated gels, for which significant negative values were obtained. Changes, affecting wires’ outer layer, negatively act on shiny appearance and luster, reducing corrosion resistance. Although examined orthodontic wires showed good chemical stability and low toxicity, surface corrosion from exposure to fluorinated agents was observed. Home use must be accompanied by clinician prescription and, for household dental gels, must follow manufacturers’ recommendations, ensuring prophylactic action without damaging alloys surfaces.
Microwave fabrication and design techniques are commonly employed in the terahertz (THz) domain. However, a characterization of commercially available microwave dielectric materials is usually ...lacking at sub-THz and THz frequencies. In this work, we characterized four substrates by Rogers and an Ordyl dry resist between 0.2 and 2 THz, in terms of relative permittivity and loss tangent. The reflectance spectra of the investigated materials were retrieved by means of THz time-domain spectroscopy in reflection mode and post-processed according to a transmission-line model in which the materials’ parameters are fit by means of the Havriliak–Negami variation of the Debye model. The relative permittivity of the investigated materials showed negligible frequency dispersion in the sub-THz and in the THz range. In terms of the loss tangent, the Rogers substrates revealed a more pronounced frequency-dispersive behavior among different materials, as dictated by the Havriliak–Negami model. The Ordyl resist was dispersive in the 0.2–1.2 THz range and presented a nearly constant loss tangent value between 1.2 and 2 THz. These results may represent a reference for the development of innovative components for THz and sub-THz emerging applications.
The purpose of the in vitro study is to investigate and compare the morphological features and the chemical stability in weight of two different polyurethane-based blends, Smart Track (LD30) and ...Exceed30 (EX30), used for orthodontic aligners manufacture before and after the oral usage.
Twenty orthodontic aligners were randomly selected: 10 LD30 and 10 EX30, each group was divided in two subgroups, never used and intra-orally aged. By the employment of a Stereomicroscope, a section of 5 × 5 mm was cut from the buccal surface of the incisal region of each aligner. All samples were subjected to Scanning Electron Microscopy and Ageing tests in different solutions to simulate the hostility of the oral environment. The statistical method used was t-test.
At SEM images, LD30 appears more homogeneous in texture respect to EX30. However, after clinical usage, both materials show significant structural alterations: findings have been supported by higher magnifications at SEM, by which it is clearly to observe many superficial cracks cross through the polymer structures of LD30U, absent in never used samples. LD30U surface becomes also smoother due to the disappearance of most of the conglomerates, but at the same time also rougher while EX30U shows a greater irregularity and porosity in which large and deep cracks are also highlighted. Although these changes occur persistently, in the aging tests no significant weight loss from both materials has been found, confirming the initial hypothesis of a good chemical stability and safety of both polyurethane mixtures even in conditions of severe hostility.
LD30 is the expression of the technological evolution of EX30, this is made evident above all by its morphological architecture, more homogeneous and defined but also by the chemical stability that can be appreciated even in evident critic situations.
Today, the key methodology to study in vitro or in vivo electrical activity in a population of electrogenic cells, under physiological or pathological conditions, is by using microelectrode array ...(MEA). While significant efforts have been devoted to develop nanostructured MEAs for improving the electrophysiological investigation in neurons and cardiomyocytes, data on the recording of the electrical activity from neuroendocrine cells with MEA technology are scarce owing to their weaker electrical signals. Disordered silicon nanowires (SiNWs) for developing a MEA that, combined with a customized acquisition board, successfully capture the electrical signals generated by the corticotrope AtT‐20 cells as a function of the extracellular calcium (Ca2+) concentration are reported. The recorded signals show a shape that clearly resembles the action potential waveform by suggesting a natural membrane penetration of the SiNWs. Additionally, the generation of synchronous signals observed under high Ca2+ content indicates the occurrence of a collective behavior in the AtT‐20 cell population. This study extends the usefulness of MEA technology to the investigation of the electrical communication in cells of the pituitary gland, crucial in controlling several essential human functions, and provides new perspectives in recording with MEA the electrical activity of excitable cells.
Based on disordered silicon nanowires, a newly designed microelectrode array (MEA) enables to record the low amplitude signals generated by a population of neuroendocrine cells of the pituitary gland. The method here provides an effective tool for exploring the complexity of the neuroendocrine system and new perspectives for MEA technology.