The objective of this study was to determine the mechanical strength of Peltophorum dubium (Spreng.) Taub. wood the fiber saturation point (FSP≈30%) and equilibrium moisture content (TUeq≈12%), ...trying to correlate and establish models of equations that explain these characteristics. For this, we sampled six trees, where the positionsfrom 0,30 m to 1,30 m concocted in the materials for the testing of mechanical impact resistance and static bending, with dimensions of 2,0 x 2,0 x 30,0 cm. The results obtained in the impact resistance can see that the values of W, K, and the CD timber FSP were higherthan the TUeq in 1,94, 1,82 and 1,36 times, respectively, since the static bending mean values of MOE and MOR of wood to TUeq were larger than the FSP, at about 1,27 and 1,45 times, respectively. The mechanical strength of canafístula wood followed the trend found for other species, in which the impact resistance and static bending, rise and fall with the addition of moisture from the wood, respectively. Both trials showed a significant relationship withdensity for the FSP and the TUeq, indicating that it is possible to predict their behavior based on this variable.
Tese (doutorado) - Universidade de São Paulo, Escola Superior de Agricultura "Luiz de Queiroz", Piracicaba, 2015.
Made available in DSpace on 2017-08-28T16:13:12Z (GMT). No. of bitstreams: 1
...338811.pdf: 2172172 bytes, checksum: 83b25fbe32336d5e22e9ee56f9c0f86f (MD5)
Previous issue date: 2015
O presente estudo teve por objetivo determinar as propriedades tecnológicas da madeira de paricá, obtida de árvores de Schizolobium amazonicum Huber ex Ducke aos 14 anos provenientes de duas diferentes áreas de florestas plantadas no estado de Rondônia. Foi amostrado a campo um total de oito árvores, sendo quatro de cada um dos plantios, nos municípios de Rolim de Moura e Parecis. De cada árvore foram obtidas duas toras subsequentes com comprimento de 2,0 m, definidas após a extração de discos removidos ao longo de três posições longitudinais, que foram empregados na determinação da variação radial das características de fibras e vasos e composição química da madeira, e na variação longitudinal da densidade básica e na massa específica aparente, esta última por meio da densitometria de raios x. Da primeira tora foi determinado o rendimento em laminação e das lâminas geradas, produzidos painéis compensados que foram avaliados quanto ao desempenho físico-mecânico. Da segunda tora amostrada, foram confeccionados corpos de prova das porções próximas à medula e casca para a caracterização mecânica da madeira sólida. Os resultados obtidos mostraram que tanto o comprimento das fibras como a espessura de parede celular tenderam a um aumento gradativo, com estabilização na posição a 75% do raio em ambos os plantios amostrados. Ao longo da distância radial a madeira proveniente da área de solo de textura argilosa (Rolim de Moura) tendeu sempre a apresentar valores mais elevados de diâmetro de vasos e área ocupada em relação à madeira da área de solo de textura média e de maior compactação (Parecis), resultando em efeito da proveniência. O teor de cinzas diferiu-se entre as duas áreas, sendo maior na madeira proveniente de Parecis. A densidade básica e massa específica aparente não sofreram influência da proveniência, e mostraram tendência de redução ao longo da porção longitudinal avaliada. Houve influência somente da posição radial nas propriedades mecânicas da madeira, com a maior diferença para o MOE em flexão estática. O rendimento efetivo da laminação das toras foi próximo de 72%, e as propriedades mecânicas dos painéis compensados produzidos tornam os mesmos aptos para aplicação estrutural e naval, segundo normatização relativa a este tipo de produto. Tomando-se por base a variação radial dos parâmetros de comprimento e espessura de parede das fibras, já se observa a presença de madeira adulta no S. amazonicum aos 14 anos nas condições de crescimento avaliadas. Embora os coeficientes indicativos de qualidade das fibras comprovem o potencial da espécie na produção de polpa e papel na idade considerada, o elevado teor de extrativos deve ser considerado nos programas de melhoramento genético. Com exceção da resistência ao cisalhamento, a madeira de paricá aos 14 anos apresentou um incremento nos valores de propriedades mecânicas em relação a outros estudos com esta espécie, principalmente no que se refere à rigidez de sua madeira ao esforço de flexão estática. O rendimento encontrado na laminação e as propriedades dos painéis confirmam a aptidão da espécie na manufatura de compensados.
Abstract : This research aimed to determine the technological properties of the paricá wood obtained from Schizolobium amazonicum Huber ex Ducke trees at age 14 from two different areas of planted forests in Rondônia, Brasil. It was sampled in field a total of eight trees, being four of each one of the plantations in the cities of Rolim de Moura and Parecis. Two subsequent logs with a length of 2.0 m were obtained from each tree defined after the extraction of the disks removed along of three longitudinal positions, which were used for determining the radial variation characteristics of the fibers and vessels and chemical composition of the wood, in the longitudinal variation of the basic density and in the apparent specific mass, being this one by an x-ray densitometry. The first log was determined the yield generated in the peeling process and veneers, producing plywood panels that were evaluated for physical and mechanical performance. From the second log sampled, test pieces of the portions near the cord and bark were made for the mechanical characterization of the solid wood. The obtained results show that both the length of the fiber as the cell wall thickness tended to a gradual increase with stabilization at 75% from the radius in both sampled plantations. Along the radial distance, the wood from the clay ground area (Rolim de Moura) has always tended to show higher values of diameter of vessels and occupied area in relation to the wood ground area of medium texture and higher compaction (Parecis), resulting in effect of the origin. The ash content was granted in two areas, being higher in the wood from Parecis. The density and specific gravity were not affected by the origin of wood, and tended to decrease along the longitudinal portion. There was only influence of the radial position on the mechanical properties of wood, only, with the biggest difference for the MOE in bending. The actual yield of the logs lamination was around 72%, and the mechanical properties of plywood produced make them them suitable for structural and marine applications, according to standardization concerning this type of product. Based on the radial variation of the parameters of length and wall thickness of the fibers, it is observed the presence of mature wood in S. amazonicum at age 14 in the evaluated growing conditions. Though the indicative coefficients of the quality of the fibers demonstrate the potential of the species in the production of pulp and paper at the age considered, the high content of extractives should be considered in breeding programs. Except for the shear strength wood paricá at age 14 showed an increase in the values of mechanical properties relative to other studies of this species, particularly in regard to the rigidity of its wood to bending stress. The yield found in the lamination and properties of panels confirm the suitability of the species in the manufacturing of plywood.
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior
This study investigated the effect of thermal treatment technique, used in two treatment conditions: treated wood in an autoclave and after ...conditioning, subject to the treatment under electric heater (combination), and treated wood by using only electric kiln (oven) on mechanical, hygroscopic and biological properties of Pinus taeda L. and Eucalyptus grandis W. Hill ex Maiden woods, comparing them with the results obtained for the untreated wood. For that three trees with 25 years, were deployed for each species from which it drew the first two logs for making the samples used in the evaluations. In the combination treatment these parts were subjected to thermo treatment by autoclaving at 130°C/ ± 3°C and pressure of 2 kgf/ cm² for 3 hours and after a conditioning period, subjected to electric heat in an oven at 160°C/ ± 1°C for the same period, already parts for just treatment in oven were exposed the last condition. The physical properties consisted in the evaluation of weight loss and specific weight assigned to treatment, equilibrium moisture content, rate of water absorption, effectiveness of water repellency, anti swelling efficiency, tangential, radial, and volumetric swelling and coefficient of anisotropy, the mechanical properties consisted in evaluating the modulus of elasticity and rupture in bending, maximum resistance to compression parallel, Janka hardness, impact resistance, and finally to the biological was employed accelerated decay test in the laboratory using white rot fungi and brown. The effect of heat treatment employed in the two methodologies resulted in different effects than expected with regard to the mechanical and biological. The results indicated that heat treatments used were effective in reducing the hygroscopicity and increased dimensional stability of both species, the best results for the combination method. To provide the mechanical properties of different effects, reaching an increase of resistance to certain properties and for durability of biological parts, treatments favored decay fungi employees, more pronounced effect for the combined method.
A presente pesquisa objetivou investigar o efeito da técnica de retificação térmica, empregada sob duas condições de tratamento: madeira tratada em autoclave e após condicionamento, submetida ao tratamento em estufa (combinação), e madeira tratada pelo uso de estufa elétrica apenas (estufa), nas propriedades mecânicas, higroscópicas e biológicas das madeiras de Pinus taeda L. e Eucalyptus grandis W. Hill ex Maiden, comparando-as com os resultados obtidos para a madeira sem tratamento. Para tanto, foram amostradas três árvores com 25 anos, para cada espécie, de onde se extraíram as duas primeiras toras, para confecção dos corpos de prova utilizados nas avaliações. No tratamento de combinação, as peças foram submetidas a termorretificação em autoclave a 130ºC/±3°C e pressão de 2 kgf/cm², por 3 horas e, após um período de condicionamento, submetidas ao calor em estufa elétrica a 160°C/±1°C, pelo mesmo período; já as peças destinadas apenas ao tratamento em estufa foram submetidas a última condição. As propriedades físicas consistiram na avaliação da perda de peso e massa específica, atribuída ao tratamento, umidade de equilíbrio, taxa de absorção de água, efetividade de repelência à água, eficiência anti inchamento, inchamento tangencial, radial, volumétrico e coeficiente de anisotropia; as propriedades mecânicas consistiram na avaliação do módulo de elasticidade e ruptura em flexão estática, resistência máxima à compressão paralela, dureza de Janka, resistência ao impacto; por fim, para as propriedades biológicas, empregou-se o ensaio de apodrecimento acelerado em laboratório, utilizando fungos de podridão branca e parda. O efeito do tratamento térmico empregado sob as duas metodologias, provocaram resultados diferentes do esperado, no que se refere as propriedades mecânicas e biológicas. Os resultados obtidos indicaram que os tratamentos térmicos empregados, foram eficientes na redução da higroscopicidade e aumento da estabilidade dimensional de ambas as espécies, com os melhores resultados obtidos pelo método de combinação. Para as propriedades mecânicas, os tratamentos térmicos promoveram efeitos diversos, chegando a um incremento da resistência para certas propriedades e, em relação à durabilidade biológica das peças, os tratamentos favoreceram o apodrecimento aos fungos empregados, efeito mais pronunciado para o método combinado.