Effects of impurities in Alloy 800 on the grain boundary diffusion and high temperature creep = Vpliv nečistoč v zlitini 800 na difuzijo po mejah zrn in na visoko temperaturno lezenjeLindemann, Janine ...Industrial Alloy 800 in different specifications and melts of Alloy 800 with addition od P and S were investigated using diffusion, segregation and creep measurements to reveal the influence of the ... impurities and to find relations between microstructures, creep properties and self-diffusivity. Using the radioactive tracer sectioning method the bulk and grain boundary diffusion of ▫$^{59}Fe$▫ was determined in Alloy 800 in the temperature range 800 to 1000°C. In Alloy 800H the activation energy of grain boundary diffusion of ▫$^{59}Fe$▫ is (209▫$\pm$▫17) kJ/mol. The use of the approximation of Suzuoka was confirmed by autoradiographs. Dissolved elements especially P increased the activation energy on the grain boundary diffusion of Fe by their segregation to the grain boundaries and by increasing carbide precipitation at the grain boundaries. The same materials - aged at 800°C for 100 h - were usedfor creep experiments under constant load and constant temperature. The chemical composition of the creep cavities and grain boundaries were analysed by Auger electron spectroscopy (AES). For Alloy 800 + 0.09 wt-% P an enrichment of about 14 at-% P was observed at the grain boundaries. No correlation of creep cavity formation and diffusivity could be found. The addition of P clearly enhances the creep strength of Alloy 800; this can be explained by phosphides in the grains and by enhanced precipitation of ▫$Cr_{23}C_6$▫ on the grain boundaries during the creep process.Vir: Kovine zlitine tehnologije = Metals alloys technologies. - ISSN 1318-0010 (Letn. 32, št. 6, 1998, str. 475-480)Vrsta gradiva - članek, sestavni del ; neleposlovje za odrasleLeto - 1998Jezik - angleškiCOBISS.SI-ID - 91050
Avtor
Lindemann, Janine |
Hennesen, K. |
Derder, C. |
Viefhaus, Helmut |
Grabke, Hans Jürgen
Teme
alloy 800 |
difuzija po mejah zrn |
Suzouka razlaga |
metoda presekov |
radioaktivne preiskave |
rezidualna aktivnost |
difuzija v osnovnem materialu |
fosfor |
fosfidi |
žveplo |
segregacije |
procesi lezenja |
jamice pri lezenju |
alloy 800 |
grain boundary diffusion |
solution of Suzuoka |
sectioning method |
radioactive traces |
residual activity |
bulk diffusion |
phosphorous |
phosphides |
sulphur |
segregation |
creep process |
creep cavities |
minimum creep strain rate
vir: Kovine zlitine tehnologije = Metals alloys technologies. - ISSN 1318-0010 (Letn. 32, št. 6, 1998, str. 475-480)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Obvestilo
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Mesto prevzema | Status gradiva | Rezervacija |
---|
Prosimo, počakajte trenutek.