YU, Xiao-Xiang; WEINBERGER, Christopher R; THOMPSON, Gregory B
Acta materialia, 11/2014, Letnik: 80Journal Article
Using a variable-composition ab initio evolutionary algorithm, the stability of various tantalum carbide compounds at ambient pressure and at 0K was investigated. The results revealed that TaC, Ta6C5 and Ta2C are the lowest energy configurations, with Ta4C3 and Ta3C2 having slightly higher energies. The vacancy ordered Ta6C5 phase had three energetically degenerate structures. A competition between the vacancy ordered and stacking fault variation of the phases was seen, with the latter becoming more favorable with lower carbon content. The close formation enthalpy of each stable and metastable phase appears to "frustrate" the carbide in the co-precipitation of multiple phases for substoichiometric compositions. Density functional theory calculations also provided the elastic constants for each of the stable and metastable phases. As the carbon content increased, the elastic constant values increased. This was associated with the change in metallic to more covalent bonding of the carbide from the density of states. The collective results of this computational work provide insight into why specific tantalum carbide phases form and the consequences they have on microstructure and properties.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.