Lee, Jeong Woo; Hall, Anthony S; Kim, Jong-Duk; Mallouk, Thomas E
Chemistry of materials, 03/2012, Letnik: 24, Številka: 6Journal Article
Graphene/Mn3O4 composites were prepared by a simple hydrothermal process from KMnO4 using ethylene glycol as a reducing agent. Mn3O4 nanorods of 100 nm to 1 μm length were observed to be well-dispersed on graphene sheets. To assess the properties of these materials for use in supercapacitors, cyclic voltammetry and galvanostatic charging–discharging measurements were performed. Graphene/Mn3O4 composites could be charged and discharged faster and had higher capacitance than free Mn3O4 nanorods. The capacitance of the composites was 100% retained after 10 000 cycles at a charging rate of 5 A/g.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.