Nalbandyan, Vladimir B.; Vasilchikova, Tatyana M.; Zakharov, Konstantin V.; Vasiliev, Alexander N.; Evstigneeva, Maria A.; Guda, Alexander A.
Inorganic chemistry, 06/2024, Letnik: 63, Številka: 22Journal Article
The homogeneous high-entropy wolframite-type solid solution (Mn1/5Co1/5Ni1/5Cu1/5Cd1/5)WO4 was prepared by solid-state reaction at 1000 °C. Elongated “crystals” were grown from the Na2WO4 flux, but their strongly broadened powder X-ray diffraction patterns indicated partial dissolution. Nevertheless, successive annealing of the homogeneous solid solution for 3–4 h at 800, 700, and 600 °C did not bring any sign of dissolution. Thus, the material is kinetically stable at low temperatures although thermodynamically unstable. The long-range antiferromagnetic order was established at T N ∼ 24.8 K. Based on magnetization and specific heat measurements, a magnetic phase diagram was built, demonstrating the presence of an additional field-induced phase. In contrast to the parent MnWO4, no dielectric anomaly has been found down to 2 K.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.