Sim, Soojin; Oh, Pilgun; Park, Soojin; Cho, Jaephil
Advanced materials (Weinheim), August 27, 2013, Letnik: 25, Številka: 32Journal Article
Amorphous SiO2 coating layers with thicknesses of ca. 2, 7, 10, and 15 nm are introduced into bulk@nanowire core@shell Si particles via direct thermal oxidation at 650–850 °C. Of the coated samples, Si with a coating thickness of ca. 7 nm has the best electrochemical performance. This sample shows an initial discharge capacity of 2279 mA h g−1 with a Coulombic efficiency of 92% and displays 83% capacity retention after 50 cycles at 0.2C rate.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.