Rath, Purna Chandra; Liu, Ming-Song; Lo, Shih-Ting; Dhaka, Rajendra S.; Bresser, Dominic; Yang, Chun-Chen; Lee, Sheng-Wei; Chang, Jeng-Kuei
ACS applied materials & interfaces, 03/2023, Letnik: 15, Številka: 12Journal Article
Solid-state lithium-metal batteries have great potential to simultaneously achieve high safety and high energy density for energy storage. However, the low ionic conductivity of the solid electrolyte and large electrode/electrolyte interfacial impedance are bottlenecks. A composite solid electrolyte (CSE) that integrates electrospun Li0.33La0.557TiO3 (LLTO) nanofibers, poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP), and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) is fabricated in this work. The effects of the LLTO filler fraction and morphology (spherical vs fibrous) on CSE conductivity are examined. Additionally, a fluorine-rich interlayer based on succinonitrile, fluoroethylene carbonate, and LiTFSI, denoted as succinonitrile interlayer (SNI), is developed to reduce the large interfacial impedance. The use of SNI rather than a conventional ester-based interlayer (EBI) effectively decreases the Li//CSE interfacial resistance and suppresses unfavorable interfacial side reactions. The LiF- and CF x -rich solid electrolyte interphase (SEI), derived from SNI, on the Li metal electrode, mitigates the accumulation of dead Li and excessive SEI. Importantly, dehydrofluorination reactions of PVDF-HFP are significantly reduced by the introduction of SNI. A symmetric Li//CSE//Li cell with SNI exhibits a much longer cycle life than that of an EBI counterpart. A Li//CSE@SNI//LiFePO4 cell shows specific capacities of 150 and 112 mAh g–1 at 0.1 and 2 C (based on LiFePO4), respectively. After 100 charge–discharge cycles, 98% of the initial capacity is retained.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.