YAMANE, H; SHIBATA, M; SHIMANE, Y; JUNKE, T; SEINO, Y; ADAMS, S; MINAMI, K; HAYASHI, A; TATSUMISAGO, M
Solid state ionics, 06/2007, Letnik: 178, Številka: 15-18Journal Article
A synchrotron X-ray powder diffraction pattern was measured for a lithium superionic conductor, Li7P3S11, which has a high conductivity of 3.2X10-3Scm-1 at room temperature and a low activation energy of 12kJmol-1 Mizuno et al., Solid State Ionics, vol. 177 (2006) 2721. The crystal structure was solved by a direct space global optimization technique and refined by the Rietveld method. The compound crystallizes in a triclinic cell, space group P-1, a=12.5009(3) A, b=6.03160(17) A, c=12.5303(3) A, alpha=102.845(3) deg , beta=113.2024(18) deg , gamma=74.467(3) deg . PS4 tetrahedra and P2S7 ditetrahedra are contained in the structure and Li ions are situated between them.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.