Godec, M; Sustarsic, B; Jenko, M
Metalurgija, 01/2008, Letnik: 47, Številka: 1Journal Article
We produced amorphous Fe-Si-B soft-magnetic powder using water atomisation. During annealing the powder particles developed a nanocrystalline structure, and annealing at over 700 deg C led to the formation of ferrite and boride phases. Here we present a high-magnification electron backscatter diffraction (EBSD) mapping analysis of the powder particles, in combination with a field-emission-gun scanning electron microscopy (FEGSEM) analysis. Some of the problems associated with the preparation of the powder particles for the EBSD analysis as well as the drift problems occurring during the EBSD mapping are reported.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.