Zhang, Ye; Guo, Jiangna; Xu, Dan; Sun, Yi; Yan, Feng
ACS applied materials & interfaces, 08/2017, Letnik: 9, Številka: 30Journal Article
Metal nanowires (NWs) have become the most promising candidates for the next generation of flexible transparent conductive electrodes (FTCEs), with high transmittance and low sheet resistance. In this work, ultralong silver NWs (Ag NWs), ∼220 μm (even larger than 400 μm) in length and ∼55 nm in diameter (aspect ratio: ∼4000), were synthesized via a one-pot polyol process using high molecular weight poly(vinylpyrrolidone) (M w = 1 300 000) and an appropriate concentration of FeCl3 (12.5 μM) through hydrothermal reaction. The prepared Ag NWs were purified by a filter cloth (pore size: about 30 × 50 μm2) to remove the Ag nanoparticles and short-length Ag NWs. The FTCE based on the ultralong Ag NWs without any post-treatments exhibits low sheet resistance of 155.0 Ω sq–1 and transmittance of 97.70% at 550 nm. The outstanding performance of FTECs demonstrated that the ultralong Ag NWs are ideal materials for applications in flexible transparent optical devices.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.