Qi, Haisong; Cai, Jie; Zhang, Lina; Kuga, Shigenori
Biomacromolecules, 06/2009, Letnik: 10, Številka: 6Journal Article
All-cellulose composite films were prepared, for the first time, from native cellulose nanowhiskers and cellulose matrix regenerated from aqueous NaOH−urea solvent system on the basis of their temperature-dependent solubility. The cellulose whiskers retained their needlelike morphology with mean length and diameter of 300 and 21 nm as well as native crystallinity when added to the latter solution at ambient temperature. The structure and physical properties of the nanocomposite films were characterized by scanning electron microscope, X-ray diffraction, and tensile tests. The composite films were isotropic and transparent to visible light and showed good mechanical properties as a result of the reinforcement by the whiskers. By varying the ratio of the cellulose whiskers to regenerated cellulose matrix (cellulose II), the tensile strength and elastic modulus of the nanocomposite films could be tuned to reach 124 MPa and 5 GPa, respectively. The tensile strength of the nanocomposite films could reach 157 MPa through a simple drawing process, with the calculated Hermans’ orientation parameter of 0.30. This work provided a novel pathway for the preparation of biodegradable all-cellulose nanocomposites, which are expected to be useful as biomaterials and food ingredients.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.