Yin, Chao; Terentyev, Dmitry; Pardoen, Thomas; Petrov, Roumen; Tong, Zhenfeng
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 03/2019, Letnik: 750Journal Article
The evaluation of the fracture toughness of tungsten is required for the design of plasma-facing components in order to ensure safe and durable operation in ITER reactor, being under construction in France. During operation, plasma facing materials will be exposed to cyclic thermo-mechanical loads combined with high energy neutron flux, which, in general, reduce the fracture toughness. Characterization of the degradation of the mechanical properties after exposure to the neutron flux involves time consuming and expensive procedures due to nuclear activation and special handling. Subsequently, development of sample miniaturization and protocols to reduce the volume of material under inspection is critical to speed up the progress in R&D. In this work, we propose a combined approach for the reconstruction of the fracture toughness – temperature curve, which is applied in the ductile to brittle transition temperature range. The approach consists of two steps: (i) application of the three point bending tests using miniaturized samples to reveal the transition temperature range on the basis of flexural strain data; (ii) execution of standardized fracture toughness tests at the upper temperature of the transition regime. The results allow the determination of the fracture toughness as a function of temperature with a reasonable accuracy. The validity of the approach has been demonstrated on two commercial tungsten grades produced according to ITER specification and tested in the as-fabricated state. The conclusions are supported by microstructural analysis performed on both standardized and miniaturized samples.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.