Zhang, Qingfeng; Jiang, Shenglin; Zeng, Yike; Fan, Maoyan; Wang, Qingping; Zhang, Guangzu; Zhang, Yangyang; Yu, Yan; Wang, Jing
Applied physics. A, Materials science & processing, 06/2011, Letnik: 103, Številka: 4Journal Article
(Pb 0.87 La 0.02 Ba 0.1 )(Zr 0.7 Sn 0.3− x Ti x )O 3 (PLBZST, 0.06≤ x ≤0.09) antiferroelectric ceramics were fabricated by conventional solid state reaction process, and their ferroelectric, dielectric, and pyroelectric properties were systemically investigated. PLBZST with different Ti content were all confirmed to be in an antiferroelectric phase at T =50°C, which is close to the lowest phase transition temperature. Compared with conventional FE ceramics, PLBZST antiferroelectric ceramics exhibited higher electric field induced pyroelectric coefficient ( p ). As the content of Ti increased from 0.06 to 0.09, the pyroelectric coefficient increased from 1000 to 6500 μC/m 2 K under a 500 V/mm DC bias field. The maximum pyroelectric coefficient of 8400 μC/m 2 K was obtained at x =0.09 when an 850 V/mm DC bias field was applied, which is far larger than that of conventional phase transition pyroelectric materials. Large pyroelectric response is beneficial for the development of infrared detectors and thermal imaging sensors.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.