Huang, A.H.; Wang, Y.F.; Wang, M.S.; Song, L.Y.; Li, Y.S.; Gao, L.; Huang, C.X.; Zhu, Y.T.
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 02/2019, Letnik: 746Journal Article
A high performance Cu-Cr-Zr alloy with an ultimate tensile strength of 612 MPa, a uniform elongation of 5% and an electrical conductivity of 84.7% IACS was achieved by the severe rotary swaging and two-step peak-aging treatment. A perfect ultrafine grained microstructure with uniformly distributed nano-precipitates was identified to be responsible for the excellent properties of the studied alloy. The proposed method of rotary swaging in combination with the two-step aging treatment shows good potential for producing the high performance Cu-Cr-Zr alloy, which can not only fulfill the industrial requirement of strength and electrical conductivity, but also is suitable for mass production.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.