Chen, Mohan; Ding, Ji Cheng; Kwon, Se-Hun; Wang, Qimin; Zhang, Shihong
Corrosion science, March 2022, 2022-03-00, 20220301, Letnik: 196Journal Article
NbN coatings were deposited by multi-arc ion plating at different nitrogen partial pressure (PN) to improve the corrosion resistance and conductivity of metallic bipolar plates. With increasing PN, the phase composition of the coating transformed from a mixture of β-Nb2N and δ’-NbN to δ-NbN, which was accompanied by grain refinement. The coating deposited at a relatively high PN (3.5 Pa) exhibited the lowest ICR and corrosion current density of 12.75 mΩ·cm2 and 2.619 × 10−6 A/cm2, respectively. The influence of the phase composition, microstructure, and surface morphology on the anti-corrosion behavior and conductivity of the coating were analyzed in detail. •NbN coatings were deposited by multi-arc ion plating at various nitrogen partial pressures.•The NbN coating deposited at a relatively high nitrogen partial pressure possessed better properties.•The influence of the phase composition, microstructure, and morphology on the properties of the coated-SS were analyzed.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.