Ding, Jian; Zhang, Pan; Li, Xingwen; Wang, Lisheng; Liao, Wenzhe; Huang, Lixin; Xia, Xingchuan
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 04/2018, Letnik: 723Journal Article
In this work, trace amount of scandium element (Sc, 0.2 wt. %) was added to investigate microstructure and thermal stability evolution behavior of Sc-containing A356.2 alloy by using cyclic thermal exposure method. OM, SEM, TEM and image analysis software were applied to evaluate microstructure evolution. The results showed that both secondary dendrite arm spacing (SDAS) and average area of eutectic silicon increased with exposure temperature and exposure time increasing. In addition, thermal stabilities of ultimate tensile strength (UTS), yield strength (YS), elongation (EI) and micro-hardness were sensitive to cyclic thermal exposure temperatures. E.g., under 200°C exposure temperature, more than 6 cycles were needed for the mechanical properties getting stable, and with exposure temperature of 250°C about 4 cycles were needed. While, for exposure temperatures of 300°C and 350°C, only 2 cycles were needed. Precipitation mechanisms of Nano Si (syn) phase and Al3Sc phase inside of grains were discussed, and comprehensive effect of Al3Sc, Nano Si (syn) phase, SDAS and eutectic silicon was responsible for the thermal stability of the alloy under cyclic thermal exposure conditions.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.