Maggio, Mario; Marrazzo, Rosamaria; Acocella, Maria Rosaria; Granata, Veronica; Guerra, Gaetano
Carbon (New York), 02/2018, Letnik: 127Journal Article
Oxidized Carbon Nanotubes (CNT) form stable adducts with ammonium ions exhibiting long alkyl chains. Outer surfaces of CNT adducts are completely covered by hydrocarbon tails, which spontaneously organize in hexagonal rotator order, with 1 hydrocarbon tail per 8 graphitic carbon atoms of the external CNT wall. Order-disorder transitions, which involve loss of packing and of zig-zag planar conformation of the bound hydrocarbon tails, occur by heating at temperatures not far from room temperature and lead to temperature-triggered dispersion in organic media of the CNT adducts. CNT adduct formation is reversible with pH changes, as clearly shown by reversible moving of CNT between apolar and polar immiscible phases. Display omitted
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.