Werinos, M.; Antrekowitsch, H.; Ebner, T.; Prillhofer, R.; Uggowitzer, P.J.; Pogatscher, S.
Materials & design, 10/2016, Letnik: 107Journal Article
This study first provides a concise review of natural aging in Al–Mg–Si alloys and its effect on artificial aging. The second part investigates prolonged natural aging at different temperatures for >500days of commercial and trace element added alloys. Together, the two parts improve the picture of underlying mechanisms and refine suggestions regarding the five stages of natural aging. Trace Sn- or Sn+In-added alloys show a trend towards higher activation energies of clustering, and a higher temperature dependency of natural aging than commercial alloys. This is attributed to an additional contribution of a thermally activated vacancy release from Sn- and In-vacancy pairs. Sn and In additions are suggested to decrease cluster number density while increasing cluster size. Prolonged natural aging increasingly retards artificial aging kinetics. This is interpreted according to increasingly slower cluster dissolution kinetics and slower preferential growth of β´´ needles. The reachable strength however seems to strongly depend on the ratio and size of coarse β´´ needles, preferentially grown, and the number of fine re-precipitated β´´ needles. Artificial aging after prolonged natural aging at 45°C increases the artificial aging peak hardness due to a lower density of larger clusters than at lower temperatures. Display omitted •A refined overall mechanistic picture of natural aging of Al–Mg–Si alloys is presented.•Vacancy trapping trace elements retard natural aging (up to several years in special cases).•Trace elements increase the temperature dependency of natural aging.•Prolonged natural aging generally retards artificial aging kinetics.
Avtor
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.