Liu, B.X.; Yin, F.X.; Dai, X.L.; He, J.N.; Fang, W.; Chen, C.X.; Dong, Y.C.
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 01/2017, Letnik: 679Journal Article
The mechanical properties and fracture characteristics of stainless steel clad plates by vacuum hot rolling at different rolling temperature of 1100°C (S1), 1200°C (S2) and 1300°C (S3) are investigated in detail. The carburized layer thickness and grain size is gradually increased with the increasing rolling temperature. The sufficient alloy element diffusion, recovery and recrystallization at the bonding temperature of 1300°C lead to the highest interfacial shear strength and the lowest longitudinal tensile strength among the three clad plates. However, the tensile ductility is increased with the increasing rolling temperature, which is attributed to the increased interfacial bonding strength. The strong interface can effectively delay the formation of interfacial delamination crack and premature localized necking, resulting into a prolong uniform plastic deformation stage with a low stress triaxiality. In addition, there are many intergranular tunnel cracks with the length of 50–150µm presented in the carburized layer due to Cr23C6 carbides on the grain boundary, which can effectively toughen the stainless steel clad plates.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.