Wei, Simin; Qin, Nailing; Wu, Guiying; Xu, Zhengbing; Miao, Lei; Chen, Xiyong; Yan, Jialin
Materials, 02/2024, Letnik: 17, Številka: 5Journal Article
Bi-based YbMg2Bi1.98 Zintl compounds represent promising thermoelectric materials. Precise composition and appropriate doping are of great importance for this complex semiconductor. Here, the influence of Zn substitution for Mg on the microstructure and thermoelectric properties of p-type YbMg1.85−xZnxBi1.98 (x = 0, 0.05, 0.08, 0.13, 0.23) was investigated. Polycrystalline samples were prepared using induction melting and densified with spark plasma sintering. X-ray diffraction confirmed that the major phase of the samples possesses the trigonal CaAl2Si2-type crystal structure, and SEM/EDS indicated the presence of minor secondary phases. The electrical conductivity increases and the lattice thermal conductivity decreases with more Zn doping in YbMg1.85−xZnxBi1.98, whereas the Seebeck coefficient has a large reduction. The band gap decreases with increasing Zn concentration and leads to bipolar conduction, resulting in an increase in the thermal conductivity at higher temperatures. Figure of merit ZT values of 0.51 and 0.49 were found for the samples with x = 0 and 0.05 at 773 K, respectively. The maximum amount of Zn doping is suggested to be less than x = 0.1.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.