Tacikowski, M.; Kamiński, J.; Rudnicki, J.; Borowski, T.; Trzaska, M.; Wierzchoń, T.
Vacuum, 03/2011, Letnik: 85, Številka: 10Journal Article
The layers based on chromium nitride were produced on the AZ91D magnesium alloy using a hybrid surface treatment. The treatment consists of nitriding of the chromium-precoated magnesium alloy. The proposed treatment yields diffusive, composite gradient-type chromium nitride layers which are diffusion-bonded to the substrate. The effect of these layers on the corrosion behavior of the AZ91D magnesium alloy was investigated by the potentiodynamic and impedance spectrometry methods. It was found that the formation of the diffusive, composite chromium nitride layers on the AZ91D alloy may result in a significant decrease of the corrosion activity measured by the corrosion potential. This effect is correlated with the layer thickness and becomes significant with relatively thin layers (less than 1 μm thick). Moreover, with the thin layers the impedance modulus is the highest and phase angle has a beneficial character. ► Hybrid method allows to produce diffusive chromium nitride layers on magnesium alloys. ► Chromium nitride layers on AZ91D alloy improve corrosion resistance. ► The best corrosion resistance occur when the CrN layers are sufficiently thin.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.