The novel synthesis of MgO from Laurus nobilis L. leaves was prepared using the green synthesis method. It is using direct blending process to decorate MgO/PEG nanocomposite to enhance the photodegradation properties and examine its physical properties using diverse characterization techniques, including XRD, FTIR, SEM, EDX, and UV–Vis. X-ray diffraction reveals a cubic phase of MgO with a 37-nm grain size. SEM images confirm spherical nanoparticles with a diameter size of 22.9 nm. The optical energy gap of MgO NPs was 4.4 eV, and the MgO/PEG nanocomposite was 4.1 eV, which made it an efficient catalyst under sunlight. The photocatalytic activity of Rose Bengal (RB) and Toluidine Blue (TB) dyes at 5 × 10 −5  mol/l dye concentration indicates excellent degradation efficiencies of 98% and 95% in 120 min, respectively, under sunlight irradiation. MgO/PEG is an excellent candidate nanocomposite for applications of photodegradation and could be used for its potential capability to develop conventionally used techniques.