Budak, Ö; Geißler, M; Becker, D; Kruth, A; Quade, A; Haberkorn, R; Kickelbick, G; Etzold, B. J. M; Presser, V
ACS applied energy materials, 05/2020, Letnik: 3, Številka: 5Journal Article
Nb2O5 has been explored as a promising anode material for use as lithium-ion batteries (LIBs), but depending on the crystal structure, the specific capacity was always reported to be usually around or below 200 mAh/g. For the first time, we present coarse-grained Nb2O5 materials that significantly overcome this capacity limitation with the promise of enabling high power applications. Our work introduces coarse-grained carbide-derived Nb2O5 phases obtained either by a one-step or a two-step bulk conversion process. By in situ production of chlorine gas from metal chloride salt at ambient pressure, we obtain in just one step directly orthorhombic Nb2O5 alongside carbide-derived carbon (o-Nb2O5/CDC). In situ formation of chlorine gas from metal chloride salt under vacuum conditions yields CDC covering the remaining carbide core, which can be transformed into metal oxides covered by a carbon shell upon thermal treatment in CO2 gas. The two-step process yielded a mixed-phase tetragonal and monoclinic Nb2O5 with CDC (m-Nb2O5/CDC). Our combined diffraction and spectroscopic data confirm that carbide-derived Nb2O5 materials show disordering of the crystallographic planes caused by oxygen deficiency in the structural units and, in the case of m-Nb2O5/CDC, severe stacking faults. This defect engineering allows access to a very high specific capacity exceeding the two-electron transfer process of conventional Nb2O5. The charge storage capacities of the resulting m-Nb2O5/CDC and o-Nb2O5/CDC are, in both cases, around 300 mAh/g at a specific current of 10 mA/g, thereby, the values are significantly higher than that of the state-of-the-art for Nb2O5 as a LIB anode. Carbide-derived Nb2O5 materials also show robust cycling stability over 500 cycles with capacity fading only 24% for the sample m-Nb2O5/CDC and 28% for o-Nb2O5/CDC, suggesting low degree of expansion/compaction during lithiation and delithiation.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.