Voitsekhovskii, A. V.; Nesmelov, S. N.; Dzyadukh, S. M.; Vasil’ev, V. V.; Varavin, V. S.; Dvoretsky, S. A.; Mikhailov, N. N.; Yakushev, M. V.; Sidorov, G. Yu
Journal of communications technology & electronics, 03/2018, Letnik: 63, Številka: 3Journal Article
The impact of the presence of the near-surface graded-gap layers with an increased content of CdTe on the admittance of MIS structures based on MBE-grown n -Hg 1– x CdxTe ( x = 0.22–0.23) with the Al 2 O 3 insulating coating has been experimentally studied. It has been shown that the structures with a gradedgap layer are characterized by a deeper and wider capacitance dip in the low-frequency capacitance–voltage (CV) characteristic and by higher values of the differential resistance of the space-charge region than the structures without such a layer. It has been found that the main features of the hysteresis of capacitance dependences typical of the graded-gap structures with SiO 2 /Si 3 N 4 are also characteristic of the MIS structures with the Al 2 O 3 insulator. The factors that cause an increase in the CV characteristic hysteresis upon formation of the graded-gap layer in structures with SiO 2 /Si 3 N 4 or Al 2 O 3 are still debatable, although it may be assumed that oxygen plays a certain role in formation of this hysteresis.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.