Sawanishi, C.; Ogura, T.; Taniguchi, K.; Ikeda, R.; Oi, K.; Yasuda, K.; Hirose, A.
Science and technology of welding and joining, 20/1/1/, Letnik: 19, Številka: 1Journal Article
Dual phase 980 MPa grade (DP980) steel sheets were resistance spot welded using a pulsed current, and the effects of the pulsed current on the strength properties of the joints were investigated. The pulsed current improved the mechanical properties of the joints in cross tensile tests. In situ observations during tear tests revealed that the ductility of the nugget was improved and that the propagation of cracks into the nugget was inhibited when the pulsed current was used. Microstructural observations and electron probe microanalysis (EPMA) of the nugget showed that the segregation of phosphorus at the nugget was reduced in the joint welded using the pulsed current, suggesting that the pulsed current improved the ductility of the nugget by altering their microstructures.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.