Mishra, S.S.; Yadav, T.P.; Singh, S.P.; Singh, A.K.; Shaz, M.A.; Mukhopadhyay, N.K.; Srivastava, O.N.
Journal of alloys and compounds, 09/2020, Letnik: 834Journal Article
In present investigation, the selective removal of Al from the quasi-lattice sites of quasicrystalline alloy surface was examined in order to produce the nano-particles of metal/metal oxides within the micro-porous network. Al was selectively etched from both the as-cast as well as annealed Al63Cu25Fe12 quasicrystalline alloys through the treatment with 10 mol NaOH solution at different time interval. In the as-cast sample, higher density of porosity was observed compared to that of annealed alloy. However, dealloying specifically for 4 and 8 h yielded nano-size particles on quasicrystalline surface (of both the alloys) in which very fine particles were detected at 8 h. The increase in density and decrease in size of the nano-particles was found with dealloying duration. X-ray diffraction analysis was performed to characterize the samples. Scanning electron microscopy, transmission electron microscopy and energy dispersive X-ray analysis were carried out to investigate the surface microstructure, internal morphology and chemical composition. The chemical dealloying treatments yielded nano-particles of Cu and Fe along with their oxides on the quasicrystalline surface. Furthermore, the catalytic activity of leached quasicrystalline materials was evaluated towards degradation of non-biodegradable and hazardous methylene blue (organic dye). •The Evolution of porous structure on poly-grain Al63Cu25Fe12 quasicrystalline alloy surface.•The chemical dealloying yielded nano-particles of Cu and Fe on the quasicrystalline surface.•Excellent catalytic activity of leached quasicrystals on the degradation of methylene blue.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.