Asami, K.; Kikuchi, M.
Corrosion science, 11/2003, Letnik: 45, Številka: 11Journal Article
In-depth distribution of rusts on two weathering steels and a plain carbon steel exposed to atmosphere for 17 years under a bridge at a coastal + industrial region in Japan were studied. In the rust layer on all specimens, α-FeOOH, β-FeOOH, γ-FeOOH, Fe 3O 4 and so-called amorphous rust were found. Within rust layers, there were thick parts and thin parts, which were finely and complicatedly distributed on steels. Among these rust species, α-FeOOH was dominant on all specimens. α-FeOOH appeared almost homogeneously through the rust layer. Its concentration was higher on weathering steels than on plain carbon steel. β-FeOOH was found mainly at thick parts and was scarce at thin parts of rust layers. Concentration of α-FeOOH was higher and that of γ-FeOOH was lower on weathering steels than on plain carbon steel. Amorphous rust was located at the bottom of the rust layer irrespective of steel types. Concentration of magnetite was negatively correlated with concentration of β-FeOOH.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.